Abstract:Poly(lactic acid) (PLA) was an eco‐friendly and biodegradable material. However, its molecular chain was inflexible and showed limited toughness. In this work, PLA was modified with epoxy‐terminated hyperbranched polymer (EHBP) by melt blending to improve the toughness of PLA. The results showed that epoxy groups within EHBP reacted with carboxyl and hydroxyl groups of PLA, forming chemical micro‐crosslinking. In addition, intermolecular hydrogen bonds were formed between hydroxyl groups on EHBP and PLA, and the combined action of the two ultimately improved the toughness and strength of PLA. Chemical micro‐crosslinking was validated via Fourier transform infrared spectroscopy (FTIR) and gel content analysis. By observing the microscopic morphology of the impact fracture of the blends, it was found that the interface adhesion of the blends increased with the addition of EHBP, enhancing the corresponding mechanical properties. The best interface adhesion was achieved when 2.5 phr EHBP was added to PLA. At this point, compared with neat PLA, the maximum tensile strength, impact strength, elongation at break, and flexural modulus of PLA/EHBP increased by 17.4%, 54.5%, 107.1%, and 25.8% respectively, achieving the goal of simultaneously enhancing the toughness and strength of PLA. The simultaneous improvement in the strength and toughness of PLA expands its potential application value. Poly(lactic acid) (PLA) is an eco‐friendly and biodegradable material. However, its molecular chain was rigid and showed limited toughness. In this work, PLA was modified with epoxy‐terminated hyperbranched polymer (EHBP) by melt blending to improve the toughness. The results showed that epoxy groups within EHBP reacted with carboxyl and hydroxyl groups of PLA, forming chemical micro‐crosslinking. In addition, intermolecular hydrogen bonds were also formed between EHBP and PLA. The combined action of the above two aspects ultimately improved the toughness and strength of PLA. The mechanical property tests results showed that the mechanical properties of PLA improved best when 2.5 phr of EHBP was added. At this point, compared with neat PLA, the maximum tensile strength, impact strength, elongation at break, and flexural modulus of PLA/EHBP increased by 17.4%, 54.5%, 107.1%, and 25.8%, respectively, compared to those of neat PLA. It achieves the goal of simultaneously enhancing the toughness and strength of PLA and subsequently expands its potential application applications.

High‐toughening modification of polylactic acid by long‐chain hyperbranched polymers

Toughening Modification of Polylactic Acid by Long-Chain Hyperbranched Polymers Containing Polycaprolactone end Groups

Preparation and characterization of compatibilized and toughened polylactic acid/cellulose acetate films by long‐chain hyperbranched polymers

Synergistic toughening and reinforcement of poly(lactic acid) with epoxy‐terminated hyperbranched polymers

Enhancing toughness of poly(lactic acid) by regulating the hydroxyl value and viscosity of hydroxyl terminated polybutadiene

Synthesis and investigation of sustainable long-chain branched poly(lactic acid-r-malic acid) copolymer as toughening agent for PLA blends

Research Progress in Toughening Modification of Poly(Lactic Acid)

Design of biodegradable PLA/PBAT blends with balanced toughness and strength via interfacial compatibilization and dynamic vulcanization

Construction of highly ductile, UV-shielding polylactide/poly(butylene adipate- co -terephthalate) biocomposites with hyperbranched polysiloxane functionalized lignin as a biocompatibilizer

Toughening polylactide using epoxy-functionalized core-shell starch nanoparticles

Toughening Modification of Poly(lactic acid) via Melt Blending

High Melt Performance Poly (lactic acid) with Dual Hybrid Long Branching Chains Prepared by Chain Degradation and Restructuring

Preparation of high melt strength polypropylene by the reactive extrusion process and its foaming application

Lignin-derivable block copolymer micelle for effectively reinforcing and toughening polylactic acid

Preparation of super toughened flame-retardant polylactic acid with an in situ hyperbranched structure by reactive blending with a phosphorus-containing copolyester and hexamethylene glycidyl cyclotriphosphazene

Preparation of biodegradable PLA/PBAT blends with balanced toughness and strength by dynamic vulcanization process

High Performance Polylactide Toughened by Supertough Polyester Thermoplastic Elastomers: Properties and Mechanism

Supertoughened Polylactide Via the Addition of Low Content Poly(ε-caprolactone) and Tensile Deformation above the Glass Transition Temperature

Toughening of Polylactide with High Tensile Strength via Constructing an Integrative Physical Crosslinking Network Based on Ionic Interactions

Bio-based Polyamide-Assisted Supertoughening of Polylactide Through Hardening of the EGMA Elastomeric Domains of Much Low Amount

High-Toughness Poly(lactic Acid)/Starch Blends Prepared through Reactive Blending Plasticization and Compatibilization