Abstract:This study investigated the effect of layered double hydroxides (LDHs) on the deterioration process of cement paste in the sulfate environment. Cement pastes with the addition of original and calcined LDHs at 2.5 wt.% and 5.0 wt.% of cement were exposed to Na2SO4 solution for 360 days. The macroscopic performance of the cement paste was assessed based on mass variation, porosity, compressive strength, and content of sulfate ions. Furthermore, the microhardness, microstructures, and composition of the degraded pastes were examined using Vickers hardness (HV), mercury intrusion porosimetry (MIP), scanning electron microscope (SEM), X-ray diffraction (XRD), and thermogravimetric analysis (TGA). The results indicate that cement paste incorporated with LDHs can mitigate the corrosion caused by sulfate effectively, especially in the case of calcined LDHs (C-LDHs), which primarily increase the adsorption of sulfate. Compared with the control specimen, the 180 d compressive strength loss ratio of specimens with 2.5 wt.% and 5.0 wt.% of C-LDHs decreased by 63.66% and 80.51%, respectively. Moreover, LDHs can reduce the amount of ettringite crystals, densify the microstructure, and refine the pore structure to mitigate the cement paste's sulfate corrosion significantly. Compared with the control specimen, the 180 d harmful pore volume fraction of specimens laced with 2.5 wt.% and 5.0 wt.% C-LDHs decreased by 43.77% and 54.51%, respectively. In terms of the content of C-LDHs, an optimal content of C-LDHs could ensure the dominant effect of adsorption, while excessive C-LDHs could refine pores. In addition, Vickers hardness has an excellent correlation with compressive strength, which could precisely predict the compressive strength. Moreover, by combining the Vickers hardness distribution and content distribution of sulfate ions, the cross-section of the paste could be classified into four regions to evaluate the deterioration process accurately: the degraded zone, the strengthened zone, the invaded zone, and the intact zone.

Relevance of Specific Surface of Mixed Oxide Derived from Layered Double Hydroxides on the Rheological Properties and Porosity of Cement Pastes

Research on Sustainable Development of Fine-Grained Material Cement Slurry

Effect of Ornamental Stone Waste Incorporation on the Rheology, Hydration, Microstructure, and CO2 Emissions of Ordinary Portland Cement

Evaluation of Calcium Oxide Nanoparticles from Industrial Waste on the Performance of Hardened Cement Pastes: Physicochemical Study

Effects of Dolomitic Limestone on the Properties of Magnesium Oxysulfate Cement

Effects of the addition of red ceramic, limestone filler and rice husk ash in alkali silica reaction

Behaviour and Properties of Eco-Cement Pastes Elaborated with Recycled Concrete Powder from Construction and Demolition Wastes

Feasibility of Using New Sustainable Mineral Additions for the Manufacture of Eco-Cements

Portland/Sulfoaluminate Cement Blends for the Control of Early Age Hydration and Yield Stress

Characterization and adaptability of layered double hydroxides in cement paste

Enhancing the Fresh and Early Age Performances of Portland Cement Pastes via Sol-Gel Silica Coating of Metal Oxides (Bi2O3 and Gd2O3)

Mechanical performance and thermal stability of hardened Portland cement-recycled sludge pastes containing MnFe2O4 nanoparticles

Effect of Layered Double Hydroxides on the Deterioration Process of Cement Paste under Sulfate Attack

Development of Mortars That Use Recycled Aggregates from a Sodium Silicate Process and the Influence of Graphene Oxide as a Nano-Addition

Effect of Nano-SiO2 on the Mechanical Properties, Microstructure, and Hydration Process of Cementitious Materials Incorporating Hydrophobic Admixture

The Influence of Superabsorbent Polymers and Nanosilica on the Hydration Process and Microstructure of Cementitious Mixtures

Influence of silicon-dioxide nanoparticles in cementitious mortars: verification using X-ray diffraction, thermal analysis, physical, and mechanical tests

A Novel Approach to Methoxy Polyethylene Glycol-Grafted Sulfonated Poly(maleic Anhydride-Alt-styrene) As Superplasticizers in Cement Pastes

Microstructural analysis of aerated cement pastes with fly ash, Metakaolin and Sepiolite additions

Mechanical and Durability Properties of Mortars Incorporating Red Mud, Ground Granulated Blast Furnace Slag, and Electric Arc Furnace Dust

Rheological Properties and Early-Age Microstructure of Cement Pastes with Limestone Powder, Redispersible Polymer Powder and Cellulose Ether