Surface Anticorrosion Engineering by Polyphosphate Oxyanions for Durable Seawater Oxidation
Xunlu Wang,Huashuai Hu,Junnan Song,Junqing Ma,Hanxiao Du,Jiacheng Jayden Wang,Min Wang,Wei Chen,Yin Zhou,Jiacheng Wang,Minghui Yang,Lingxia Zhang
DOI: https://doi.org/10.1002/aenm.202402883
IF: 27.8
2024-09-01
Advanced Energy Materials
Abstract:Inspired by the concept of hard and soft acids and bases, harder acid Ni>3+ sites, obtained by coordinating polyphosphate oxyanions (P3O105−), prefer adsorption of hard base OH− rather than soft base Cl− in alkaline seawater. This could significantly enhance oxygen‐evolution selectivity and inhibit undesirable chlorine oxidation, thus improving corrosion‐resistance ability and increasing long‐term stability of anodes toward alkaline seawater oxidation. Electrolysis of seawater represents great potentials for sustainable hydrogen production. However, both competitive Cl− adsorption and catalysts corrosion caused by chlorine oxidation reaction (ClOR) are major challenges in seawater electrolysis. Inspired by the concept of hard and soft acids and bases (HSAB), polyphosphate oxyanions (P3O105−) on Ni(OH)2 surface is coordinated to obtain harder acid Ni sites, which could obtain 160 times stability enhancement compared to pure Ni(OH)2 for oxygen evolution reaction (OER) in alkaline seawater at 800 mA cm−2. Also, the turnover frequency value on Ni(OH)2‐P3O105− is 50 times that on Ni(OH)2, implying higher intrinsic OER activity of Ni(OH)2‐P3O105−. Theoretical and experimental investigations show that P3O105− could facilitate transition of Ni3+ to harder acid Ni>3+, thus preferring adsorption of hard base OH− rather than soft base Cl−. This could enhance OER selectivity and inhibit undesirable ClOR. Furthermore, molecular dynamics simulations indicate that the Cl− concentration near the electrode could be reduced by nearly half due to electrostatic repulsion of Cl− by surface P3O105− oxyanions. When assembled into an electrolyzer for alkaline seawater splitting, it could operate at 2.2 V with large current up to 1.4 A for 240 h.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,energy & fuels