Abstract:Electron beam freeform fabrication (EBF3) additive manufacturing technique has been successfully employed to print the non-weldable Al-5Cu thin-walled parts through an optimized set of process parameters. Post-heat treatment is conducted to engineer the desirable microstructure containing multiple nanostructures, i.e., the nanoscale θ" and θ' precipitates, stacking faulted zones and Al-Cu-Cd clusters, leading to a high-strength Al-5Cu alloy with good ductility. The grain formation mechanisms are revealed via a combinatorial simulation and experimentation. It is shown that EBF3 process can produce three different types of grain microstructures: fully equiaxed, fully columnar, and the mixture. In the layerwise melt pool solidification process, wide partially melted zone is observed to favor the formation of equiaxed grains due to its inheritance characteristic. After solution and aging heat treatment, Al-Cu-Cd nanoclusters (∼ 2 nm in Dia.) are generated, which facilitates the formation of nanoscale stacking faulted zones (∼11 nm). Meanwhile, as heterogeneous nucleation sites, Al-Cu-Cd nanoclusters effectively promote θ'-Al2Cu phase (∼ 19 - 114 nm) precipitation to enable the coexistence with fine θ"-Al3Cu precipitates (∼ 7 - 37 nm). The multiscale microstructure, especially incorporating the newly identified nanoscale stacking faulted zones, activates multiple strengthening mechanisms. Consequently, its tensile properties at room temperature reach an ultimate tensile stress of ∼ 496.5 MPa, yield strength of ∼ 435.7 MPa, and elongation of ∼ 9.6%, which are superior to other as-cast and additively manufactured Al-Cu alloys. This work offers a promising processing route to directly fabricate high-strength near-net-shape Al-Cu alloy parts for the aerospace and automotive industries.

Characterization of Hypereutectoid Ti6Al4V–Cu Alloys Fabricated Using Electron Beam Additive Manufacturing

Microstructures and Phases in Electron Beam Additively Manufactured Ti-Al-Mo-Zr-V/CuAl9Mn2 Alloy

Additive manufacturing of titanium alloys with enhanced strength and uniform ductility via multi-element alloying

Fine Equiaxed Β Grains and Superior Tensile Property in Ti–6Al–4V Alloy Deposited by Coaxial Electron Beam Wire Feeding Additive Manufacturing

Effect of Cu-induced Eutectoid Transformation on Microstructure and Mechanical Properties of Ti–6Al–4V Alloy by Laser Wire Deposition

Effect of Ti on Microstructure and Mechanical Properties of Die-Cast Al-Mg-Zn-Si Alloy

Microstructure and Mechanical Properties of Cu-6.5%Al Alloy Deposited by Wire Arc Additive Manufacturing

Microstructure and Properties of 3D Ti-6Al-4V Articles Produced with Advanced Co-axial Electron Beam & Wire Additive Manufacturing Technology

Effect of Heat Treatment on Microstructure and Tensile Properties of Ti-6Al-4V Alloy Produced by Coaxial Electron Beam Wire Feeding Additive Manufacturing

Effect of the Addition of Cu and Al on the Microstructure, Phase Composition and Properties of a Ti-6Al-4V Alloy Obtained by Selective Laser Melting

Microstructure and mechanical properties of Al-Cu alloy during wire and arc additive manufacturing by adding micron TiB2 particles

Effect of Cu content on microstructure and properties of Ti-6Al-4V alloy fabricated by double-wire arc additive manufacturing

Deciphering the Microstructural Development and Excellent Ductility in Electron Beam Wire-Fed Additive Manufacturing of Ti-6Al-3Nb-2Zr-1Mo Alloys Based on High Deposition Rate

Precipitation Strengthening in Ni–Cu Alloys Fabricated Using Wire Arc Additive Manufacturing Technology

Multiscale microstructure containing nanometer-scale precipitations and stacking faults yields a high-strength Al-5Cu alloy by electron beam freeform fabrication

Microstructural Features and Microhardness of the Ti-6Al-4V Alloy Synthesized by Additive Plasma Wire Deposition Welding

The Effect of Copper Content on the Mechanical and Tribological Properties of Hypo-, Hyper- and Eutectoid Ti-Cu Alloys

Microstructure and Properties of Ti-6Al-4V Articles 3D-Printed with Co-axial Electron Beam and Wire Technology

Effect of Casting and Additive Manufacturing on the Microstructure and Mechanical Property of Al-Cu Composites

Microstructural evolution and mechanical properties of eutectoid Ti–7Ni alloy produced by electron beam powder bed fusion

Tribology properties of additively manufactured Ti6Al4V alloy after heat treatment