Effects of Ce addition on mechanical properties and thermal expansion behavior of Fe-36Ni Invar alloy

Qi Wang,Yanwu Dong,Zhouhua Jiang,Tao Zou,Yuxiao Liu,Yuning Wu,Haibiao Qing

DOI: https://doi.org/10.1016/j.matchar.2023.113584

IF: 4.537

2023-12-25

Materials Characterization

Abstract:To pursue superior yield strength and low thermal expansion characteristic of Fe-36Ni Invar alloy, Fe-36Ni Invar alloys containing various cerium (Ce) contents (0 wt%, 0.0050 wt%, 0.0170 wt%, and 0.0360 wt%) were prepared by vacuum induction melting, followed by the heat treatment process. With increasing Ce content, the evolution of the second-phase particles followed the sequence: MnO-MnS (0% Ce) → MnO-MnS + Ce 2 O 3 (0.0050% Ce) → Ce 2 O 3 + Ce 2 O 2 S (0.0170% Ce) → Ce 2 O 3 + Ce 2 O 2 S + Ni 5 Ce (0.0360% Ce). The results indicated that the grain size and the fraction of annealing twins ( f AT ) were fairly sensitive to the Ce content. The smallest average grain size ( d ̄ ) and the highest f AT were obtained by adding 0.0170% Ce. The small addition of Ce was beneficial to the improvement of strength and low thermal expansion behavior. In particular, 0.0170% Ce alloy achieved the optimal combination properties. However, the excessive addition of Ce (0.0360%) induced a sharp decrease in mechanical performance and an undesirable increase in the coefficient of thermal expansion (CTE). The Ni 5 Ce phase was unfavorable to the enhancement of mechanical properties and low thermal expansion behavior. Last but not least, 0.0170 wt% Ce content was advised for Fe-36Ni Invar alloy by considering the balance of strength and thermal expansion behavior.

materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing