Abstract:A novel crosslinked electrospun nanofibrous membrane with maleated lignin (ML) and poly(acrylonitrile) (PAN) is presented as a separator for lithium-ion batteries (LIBs). Alkali lignin was treated with an esterification agent of maleic anhydride, resulting in a substantial hydroxyl group conversion to enhance the reactivity and mechanical properties of the final nanofiber membranes. The maleated lignin (ML) was subsequently mixed with UV-curable formulations (up to 30% wt) containing polyethylene glycol diacrylate (PEGDA), hydrolyzed 3-(Trimethoxysilyl)propyl methacrylate (HMEMO) as crosslinkers, and poly(acrylonitrile) (PAN) as a precursor polymer. UV-electrospinning was used to fabricate PAN/ML/HMEMO/PEGDA (PMHP) crosslinked membranes. PMHP membranes made of electrospun nanofibers feature a three-dimensional (3D) porous structure with interconnected voids between the fibers. The mechanical strength of PMHP membranes with a thickness of 25 µm was enhanced by the variation of the cross-linkable formulations. The cell assembled with PMHP2 membrane (20 wt% of ML) showed the maximum ionic conductivity value of 2.79*10-3 S cm-1, which is significantly higher than that of the same cell with the liquid electrolyte and commercial Celgard 2400 (6.5*10-4 S cm-1). The enhanced LIB efficiency with PMHP2 membrane can be attributed to its high porosity, which allows better electrolyte uptake and demonstrates higher ionic conductivity. As a result, the cell assembled with LiFePO4 cathode, Li metal anode, and PMHP2 membrane had a high initial discharge specific capacity of 147 mAh g-1 at 0.1 C and exhibited outstanding rate performance. Also, it effectively limits the formation of Li dendrites over 1000 h. PMHP separators have improved chemical and physical properties, including porosity, thermal, mechanical, and electrochemical characteristics, compared with the commercial ones.

Porous PAN micro/nanofiber separators for enhanced lithium-ion battery performance

Porous PAN micro/nanofiber membranes with potential application as Lithium-ion battery separators: physical, morphological and thermal properties

Surface-modified electrospun polyacrylonitrile nano-membrane for a lithium-ion battery separator based on phase separation mechanism

High-stability core-shell structured PAN/PVDF nanofiber separator with excellent lithium-ion transport property for lithium-based battery

Photo-crosslinked lignin/PAN electrospun separator for safe lithium-ion batteries

Fabrication and Characterization of Nylon 66/PAN Nanofibrous Film Used as Separator of Lithium-Ion Battery

Electrospun PAN/cellulose composite separator for high performance lithium-ion battery

A high thermal stable pre‐oxidized polyacrylonitrile nanofiber separator for lithium‐ion battery

Preparation and Electrochemical Characterization of Ionic-Conducting Lithium Lanthanum Titanate Oxide/polyacrylonitrile Submicron Composite Fiber-Based Lithium-Ion Battery Separators

Hierarchical three-dimensional micro/nano-architecture of polyaniline nanowires wrapped-on polyimide nanofibers for high performance lithium-ion battery separators

Synthesis of polypropylene nanofiber separators for lithium-ion batteries via nanolayer coextrusion

Flexible core-shell PAN/CNTs@PVDF-HFP/Uio-66-NH 2 hybrid nanofibers membrane for advanced lithium-ion batteries separator

Fabrication of PVA/SiO2 (Nanofiber) Membranes Prepared Using Electrospinning Method for Lithium Battery Separator

Electrospun PVDF-HFP/PAN bicomponent nanofibers as separators in lithium-ion batteries with high thermal stability and electrolyte wettability

Electrospun MOF/PAN composite separator with superior electrochemical performances for high energy density lithium batteries

High safety and electrochemical performance electrospun para-aramid nanofiber composite separator for lithium-ion battery

Mussel Stimulated Modification of Flexible Janus Pan/Pvdf-Hfp Nanofiber Hybrid Membrane for Advanced Lithium-Ion Batteries Separator

Freestanding and Ultra-flexible PAN/ZIF-67 Hybrid Membrane with Controlled Porosity for High-Performance and High-Safety Lithium Batteries Separator

Orientation Gradient Architecture of Nanofibrous Separator towards Mechanical Enhancement and Ion Transport Acceleration for Lithium-Ion Batteries

PVDF/PAN Blend Separators Via Thermally Induced Phase Separation for Lithium Ion Batteries

Core–Shell Structured PAN@PU/PVDF-HFP Separators for Li-Ion Batteries