Abstract:Effective applications must be found for sulfur, a widely available and inexpensive element. Over the last decade, copolymers with unsaturated comonomers have been prepared via so-called inverse vulcanization. In this work, a sulfur copolymer with a circular and biosourced di-pyrrole compound was obtained for the first time and was used as the sole crosslinking agent of an unsaturated elastomer. Pyrrole compounds (PyCs) were synthesized via the Paal–Knorr reaction of 2,5-hexanedione (HD) and hexamethylenediamine (HMD) or ethylenediamine (EDM). The PyCs were obtained without using solvents or catalysts in high yield and with water as the only co-product. Poly(S- co -HMDP) and poly(S- co -EDP) copolymers were prepared under the typical conditions of inverse vulcanization. Throughout the entire synthetic pathway, the overall yield was up to 92% and the atom efficiency was up to 73%. The E -factor evaluated for organic compounds was almost null. The sulfur weight content in the copolymers ranged from 40% to 80% and the average number of sulfur atoms in the sequences ranged from 3 to 17. The copolymers were found to be amorphous with a glass transition temperature ranging from −2 to 38 °C, increasing with the content of the pyrrole ring. The number average molecular weight was found to be in the range from 1500 to 9000 g mol −1 . The molecular weight distribution was pretty narrow, with values lower than 2. NMR investigation suggested that the β position of the pyrrole ring reacted with sulfur atoms. A poly(S- co -HMDP) copolymer with an average sequence of 3 sulfur atoms was used as the sole crosslinking agent in a composite based on an unsaturated elastomer such as poly(styrene- co -butadiene) from anionic polymerization. More efficient crosslinking was obtained by promoting the ionic reaction of sulfur with elastomer chains by using 1,5-diazabicyclo(5.4.0)undec-7-ene. These results pave the way for the synthesis of a wide variety of sulfur copolymers with comonomers containing pyrrole rings for the sustainable crosslinking of elastomers, avoiding the use of oil-based accelerators.

Using conjugated system from natural sources for the synthesis of sulfur copolymers by bi‐function catalysts at mild temperatures

One‐Pot Construction of Sulfur‐Rich Thermoplastic Elastomers Enabled by Metal‐Free Self‐Switchable Catalysis and Air‐Assisted Coupling

Sulfur Conversion To Multifunctional Poly(O-Thiocarbamate)S Through Multicomponent Polymerizations Of Sulfur, Diols, And Diisocyanides

Thiol-Yne Click Polymerization: Regio- And Stereoselective Synthesis Of Sulfur-Rich Acetylenic Polymers With Controllable Chain Conformations And Tunable Optical Properties

Synthesis Of Sulfur-Containing Polyacetylenes And Fabrication Of Their Hybrids With Zno Nanoparticles

Inverse Vulcanization of Styrylethyltrimethoxysilane-Coated Surfaces, Particles, and Crosslinked Materials

Reverse Vulcanization of Monomers with Conjugated Bonds Double and Elemental Sulfur for S–S Bond Self-Healing Properties

Precisely Alternating Copolymerization of Episulfides and Isothiocyanates: A Practical Route to Construct Sulfur-Rich Polymers

Metal-free Access to Precise Synthesis of Sulfur-containing Polymers

Dynamic Sulfur-Rich Polymers from Elemental Sulfur and Epoxides

NaOH‐Assisted Multicomponent Reaction and Polymerizations of Elemental Sulfur, Diisocyanides, and Diols to Access Functional Poly(O‐thiocarbamate)s

Metal-Free Alternating Copolymerization of CS 2 and Oxetane

Poly(Thioether)S From Closed-System One-Pot Reaction Of Carbonyl Sulfide And Epoxides By Organic Bases

Catalyst-Free Thiol–Yne Click Polymerization: A Powerful and Facile Tool for Preparation of Functional Poly(vinylene Sulfide)s

Terpolymerization of Elemental Sulfur Waste with Propylene Oxide and Carbon Disulfide as a Strategy where Copolymerization fails

A sulfur copolymer with a pyrrole compound for the crosslinking of unsaturated elastomers

Converting inorganic sulfur into degradable thermoplastics and adhesives by copolymerization with cyclic disulfides

Ring‐Opening Terpolymerisation of Elemental Sulfur Waste with Propylene Oxide and Carbon Disulfide via Lithium Catalysis

Polymerization of elemental sulfur with various divinyl and diallyl monomers and properties of the copolymers

Easy Synthetic Access to High‐Melting Sulfurated Copolymers and their Self‐Assembling Block Polymers from Phenylisothiocyanate and Oxetane

Green conversion of carbon disulfide to degradable polydithiourethanes through catalyst-free multicomponent polymerizations of diamines, carbon disulfide and diacrylates