Abstract:As an ideal negative electrode material for next-generation high-energy-density batteries, lithium (Li) metal has received extensive attention from the global research community. However, the safety hazards and short cycle life caused by the growth of Li dendrites have seriously hampered the application of Li metal batteries. Based on electrochemical phenomena and theory, this paper discusses the mechanism of dendritic growth, dead Li formation, and full battery failure from the perspective of process, the consumption of Li ions on the surface induces concentration polarization. After the initial deposition, a relatively loose dendrite layer appears on the Li metal surface; the electrolyte can penetrate this dendrite layer to reach the dense Li metal surface. When the grown dendrites penetrate the concentration polarization layer, the interface concentration battery is short-circuited. In this case, the concentration difference battery tends to release all stored power and reach a potential balance between the high- and low-concentration regions, which causes the deposition of Li ions over the dendrites to reduce the ion concentration in the surrounding electrolyte. Meanwhile, the dissolution of Li ions that occurs at the roots of the dendrites increases the local ion concentration. This process accelerates the formation of a dead Li layer. A similar electrochemical process often occurs in columnar Li, as reported in other studies. When columnar Li is cycled several times, each Li column degenerates into a matchstick shape with a large head and thin neck. Therefore, eliminating concentration polarization is necessary for the application of columnar Li. Furthermore, in this work, concentration polarization and dendrite suppression in state-of-the-art porous host electrodes are analyzed. The larger specific surface area of the porous electrode greatly reduces the local current density on the electrode surface, which can reduce the interface concentration polarization and thus prevent dendrite growth. In charge-discharge cycling, a constant-voltage charging or shelving step is often inserted in each cycle in order to eliminate the influence of concentration polarization. However, if a dendritic layer has been formed on the Li metal surface after charging, in addition to the self-diffusion of ions, the self-discharge process of the interface concentration battery causes the detachment of the dendrite layer, thus resulting in the above-mentioned dead Li. Therefore, a larger amount of deposited Li yields a thicker Li dendritic layer, thus accelerating the capacity decay and failure of the battery, especially to those with high-capacity, high-voltage positive electrodes. The conclusions obtained in this paper can provide a theoretical basis for researchers to further explore Li metal protection strategies.

Diffusion Limited Current Density: A Watershed in Electrodeposition of Lithium Metal Anode

Insight into the Critical Role of Exchange Current Density on Electrodeposition Behavior of Lithium Metal

Role of Li‐Ion Depletion on Electrode Surface: Underlying Mechanism for Electrodeposition Behavior of Lithium Metal Anode

Realizing Holistic Charging–Discharging for Dendrite-Free Lithium Metal Anodes Via Constructing Three-Dimensional Li+ Conductive Networks

An Interconnected Silver Coated Carbon Cloth Framework As a Host to Reduce Lithium Nucleation Over-Potential for Dendrite-Free Lithium Metal Anodes

A conductive-dielectric gradient framework for stable lithium metal anode

Behavior of Lithium Metal Anodes under Various Capacity Utilization and High Current Density in Lithium Metal Batteries

Seeding Lithium Seeds Towards Uniform Lithium Deposition for Stable Lithium Metal Anodes

Uniform Li Deposition by Regulating the Initial Nucleation Barrierviaa Simple Liquid-Metal Coating for a Dendrite-Free Li–metal Anode

Toward Dendrite-Free Metallic Lithium Anodes: from Structural Design to Optimal Electrochemical Diffusion Kinetics

Li electrodeposition for energy storage: filling the gap between theory and experiment

Role of Lithiophilic Metal Sites in Lithium Metal Anodes

Influence of Interfacial Concentration Polarization on Lithium Metal Electrodeposition

Columnar Lithium Metal Deposits: the Role of Non-Aqueous Electrolyte Additive

Kinetic understanding of lithium metal electrodeposition for lithium anodes

Regulating Li transport in Li-magnesium alloy for dendrite free Li metal anode

Uniform lithiophilic layers in 3D current collectors enable ultrastable solid electrolyte interphase for high-performance lithium metal batteries

The factors that influence the electrochemical behavior of lithium metal anodes: electron transfer and Li-ion transport

Magnetohydrodynamic Interface-Rearranged Lithium Ions Distribution For Uniform Lithium Deposition And Stable Lithium Metal Anode

Lithiophilic Protective Dual Layer Enabling Stable Electrodeposition of Lithium at High Current Density

Lithium Metal Anodes for Rechargeable Batteries