Effect of Constant Longitudinal Magnetic Field on Microstructure and Tensile Behavior of Welded Joint of AZ91D Alloy
DOI: https://doi.org/10.1007/s11665-024-09668-0
IF: 2.3
2024-06-06
Journal of Materials Engineering and Performance
Abstract:This study explores the impact of an external longitudinal magnetic field on the microstructure and mechanical properties of AZ91 magnesium alloy joints by varying the intensity of the magnetic field (0, 5, 10, 15, and 20 mT). The microstructure of the magnesium alloy joints comprises the weld seam, heat-affected zone, and base metal zone. At 15 mT, the average grain size of the weld seam is found to be 15.54 μm, which is 38.23% smaller than joints welded without a magnetic field. The ultimate tensile strength, yield strength, and elongation after fracture of the weld exhibit a pattern of initial increase followed by a decrease with the magnetic field strength, attributed to the combined effects of Lorentz force and thermoelectric magnetic force. Specifically, at a magnetic field strength of 15 mT, the ultimate yield strength, tensile strength, and elongation after fracture of the joint are measured at 172.4, 317.5, and 7.58%, respectively, representing increments of 11.87, 11.84, and 2.98%. Furthermore, the fracture typically occurs near the HAZ, displaying ductile fracture characteristics on the fracture surface.In author group Yunhai Su affiliaion is not mentioned. So we process Affiliaiton 1 for this author. Kindly check and confirm.Thank you for your reminder.Yunhai Su also belongs to the School of Materials Science and Engineering at Shenyang University of Technology.
materials science, multidisciplinary