Abstract:The Er 3+ /Yb 3+ co-doped Y 4 GeO 8 crystal powders were successfully synthesized using a high-temperature solid-phase method. The crystal structure of the obtained phosphors was confirmed to be pure Y 4 GeO 8 through X-ray diffraction (XRD) analysis. A regression equation correlating Er 3+ /Yb 3+ doping concentrations with luminescent intensity was established based on the optimized theoretical model derived from experimental design. The optimal concentrations of Er 3+ and Yb 3+ under 980 nm laser excitation were determined as 7.41 and 21.34%, respectively, while under 1550 nm laser excitation, the concentrations were 2.66 and 17.42%, respectively. The fluorescence emission spectra of the up-conversion samples were measured, revealing intense green and red emissions with peaks at 542, 546, and 654 nm under 980 nm excitation, and peaks at 546, 557, and 663 nm under 1550 nm excitation. These peaks correspond to transitions from 2 H 11/2 to 4 I 15/2 , 4 S 3/2 to 4 I 15/2 , and 4 F 9/2 to 4 I 15/2 energy levels. The relationship between up-conversion luminescence and laser operating current for the optimal samples under 980 nm and 1550 nm was investigated, uncovering that up-conversion luminescence occurs through both two-photon and three-photon processes. A detailed analysis and discussion of the up-conversion luminescence mechanisms were conducted. Furthermore, the relationship between up-conversion fluorescence and temperature for the optimal samples was studied, revealing excellent temperature-sensing characteristics under 980 nm and 1550 nm laser excitations. The calculated illumination region coordinates for the optimal samples under 980 nm and 1550 nm wavelength excitations were (0.5558, 0.4362) and (0.5256, 0.4687), respectively. The research highlights the potential of rare-earth ion-doped up-conversion luminescent materials for diverse anti-counterfeiting applications. In particular, the Y 4 GeO 8 : Yb 3+ /Er 3+ phosphors, incorporating a dual-excitation mechanism, enhance the security of anti-counterfeiting strategies in multifaceted scenarios. The study underscores the promising developments in this field.

Extending the color response range of Yb3+ concentration-dependent multimodal luminescence in Yb/Er doped fluoride microrods by annealing treatment

Synthesis of NaYbF 4 :Er Nanocrystals with Controllable Size Morphology, and Multicolor Upconversion Luminescence for Anti-counterfeiting Applications

Tm 3+ mediated multicolor luminescence of NaYbF 4 :Er,Tm@NaYF 4 for advanced anti-counterfeiting

Dynamic modulation of multicolor upconversion luminescence of Er3+ via excitation pulse width

Upconversion Modulation through Pulsed Laser Excitation for Anti-counterfeiting

Dual-wavelength excited luminescence properties of NaYbF4:Er3+ for flexible anti-counterfeiting

Upconversion luminescence enhancement and color modulation in Yb3+/Er3+/Ln3+ (Ln = Tm, Ho) tri-doped YF3 microrods

Na(Y1.5 Na0.5)F6 single-crystal nanorods as multicolor luminescent materials.

Construction of active-inert core–shell structured nanocrystals for broad range multicolor upconversion luminescence

Anti-counterfeiting and Optical storage applications based on reversible modulated Down-shift Luminescence in photocoloration of MoO3: Eu3+ phosphor

Multi-Wavelength Excitable Multicolor Upconversion and Ratiometric Luminescence Thermometry of Yb3+/Er3+ Co-Doped NaYGeO4 Microcrystals

Enhancing the static green up-conversion luminescence of NaY(MoO 4 ) 2 :Yb/Er microcrystals via an annealing strategy for anti-counterfeiting applications

Achieving Excitation Wavelength-Power-Dependent Colorful Luminescence via Multiplexing of Dual Lanthanides in Fluorine Oxide Particles for Multilevel Anticounterfeiting

Dual-Wavelength Excited Intense Red Upconversion Luminescence from Er3+-Sensitized Y2O3 Nanocrystals Fabricated by Spray Flame Synthesis

Highly Efficient Three‐Photon Excited Red Emission in the Yb3+‐Er3+ Upconversion System at Low Excitation Intensities for Non‐Invasive Anti‐Counterfeiting

Na(Y<sub>1.5</sub>Na<sub>0.5</sub>)F<sub>6</sub>Single-Crystal Nanorods as Multicolor Luminescent Materials

Experimental Optimization, Design Synthesis, and Up-Conversion Luminescence Properties of Y4GeO8: Er3+/Yb3+ Red Phosphors

Simultaneously Achieving Multicolor Emission of Down‐Shifting and Up‐Conversion in Yb3+, Er3+ ‐Codoped Cs2NaGdCl6 Double Perovskites

Effective regulation of upconversion luminescence in NaErF4 and NaErF4@SiO2 core-shell particles

Dynamic manipulation of multimodal emission in Er3+-activated non-core–shell structure for optical thermometry and information security

Er3+/Tm3+ co-activated core@shell nanoarchitectures: tunable upconversion luminescence and high-security anti-counterfeiting