Dual-Wavelength Excited Intense Red Upconversion Luminescence from Er3+-Sensitized Y2O3 Nanocrystals Fabricated by Spray Flame Synthesis

Xiaofan Zhao,Zeyun Wu,Zining Yang,Xu Yang,Yiyang Zhang,Maohui Yuan,Kai Han,Changqing Song,Zongfu Jiang,Hongyan Wang,Shuiqing Li,Xiaojun Xu

DOI: https://doi.org/10.3390/nano10081475

IF: 5.3

2020-07-28

Nanomaterials

Abstract:Er3+-sensitized upconversion nanoparticles (UCNPs) have attracted great attention due to their tunable upconversion (UC) emissions, low cytotoxicity, high resistance to photobleaching and especially multiple effective excitation wavelengths. However, detailed energy conversion between Er3+ and Tm3+ ions in Y2O3 UCNPs is still a problem, especially under multi-wavelength and variable pulse width excitation. In this work, we successfully fabricated a series of Er3+-sensitized Y2O3 nanocrystals by a spray flame synthesis method with a production rate of 40.5 g h−1. The as-prepared UCNPs are a pure cubic phase with a mean size of 14 nm. Excited by both 980 and 808 nm lasers, the tunable upconversion luminescence (UCL) from Er3+ ions was achieved by increasing the Er3+ doping concentration, co-doping Tm3+ ions and extending excitation pulse-width. The investigations of the lifetimes and the laser power dependence of UC emissions further support the proposed mechanism, which provides guidance for achieving effective color control in anticounterfeiting and multiplexed labeling applications. In addition, the red UC emission at about 5 mm beneath the tissue surface was observed in an ex vivo imaging experiment under the excitation of 808 nm laser, indicating that the Y2O3:Er3+/Tm3+ UCNPs have great prospects in further biological applications.

materials science, multidisciplinary,physics, applied,nanoscience & nanotechnology,chemistry

What problem does this paper attempt to address?

The paper aims to address the following issues:

1. **Energy transfer mechanisms between Er3+ and Tm3+ ions in Y2O3 upconversion nanoparticles (UCNPs) under multi-wavelength excitation**: Although Er3+-sensitized upconversion nanoparticles have garnered extensive attention due to their tunable upconversion luminescence, low cytotoxicity, high photobleaching resistance, and multiple effective excitation wavelengths, the detailed energy transfer mechanisms between Er3+ and Tm3+ ions under multi-wavelength and varying pulse width excitation remain unclear.

2. **Efficient large-scale synthesis of highly crystalline Er3+-sensitized Y2O3 nanoparticles**: Traditional liquid-phase synthesis methods such as solvothermal and hydrothermal methods, while effective, require strict control of reaction conditions and have low productivity, limiting the practical application of high-quality UCNPs. Therefore, developing an efficient large-scale synthesis method is crucial.

The paper successfully prepared a series of Er3+-sensitized Y2O3 nanocrystals using the spray flame synthesis method and studied their tunable upconversion luminescence characteristics under 980 nm and 808 nm laser excitation. Additionally, by investigating luminescence lifetime and laser power dependence, the proposed mechanisms were further validated, providing guidance for color tuning in anti-counterfeiting and multiplexed labeling applications. The experiments also found that red upconversion luminescence was observed at approximately 5 mm from the tissue surface, indicating that these nanoparticles have great potential in biomedical applications.