Properties and reaction mechanism of phosphoric acid activated metakaolin geopolymer at varied curing temperatures

Hui Lin,Hui Liu,Yue Li,Xiangming Kong

DOI: https://doi.org/10.1016/j.cemconres.2021.106425

IF: 11.958

2021-06-01

Cement and Concrete Research

Abstract:<p>Reaction mechanism of phosphoric activated metakaolin is studied by techniques of calorimetry, ICP-OES, FTIR and NMR taking curing temperature and [H₃PO₄] as variables. A two-stage curing method including pre-curing at 40 °C for 24 h and second curing at 60/80 °C for another 24 h effectively mitigates thermal-cracking of the obtained silico-aluminate phosphate (SAP) samples, whose maximum compressive strength reaches 120 MPa. Dealumination of metakaolin in H₃PO₄ solution produces low aluminate-containing silicate units and subsequently condensation of silicate tetrahedrons occurs. Higher temperature and H₃PO₄ concentration accelerate the two processes. After complete reaction, A_VI structure from metakaolin disappears and the dissolved Al preferably forms Al_VI-O-P units. During reaction, metastable P-O-P intermediate appears in SAPs with higher P/Al ratio and finally transforms into Al-O-P structure upon PO₄³⁻ consumption. Phosphate units as P(<em>OAl</em>)_x(H₂O)_4-x are connected with Si or Al structure units. Major structural units of the SAPs include Al-O-P, Si-O-P, Si-O-Si, and Si-O-Al.</p>

construction & building technology,materials science, multidisciplinary