Preparation of a Flame-Retardant Curing Agent Based on Phytic Acid–Melamine Ion Crosslinking and Its Application in Wood Coatings

An Wei,Shunxiang Wang,Yongjin Zou,Cuili Xiang,Fen Xu,Lixian Sun

DOI: https://doi.org/10.3390/polym16111557

IF: 5

2024-05-31

Polymers

Abstract:To broaden the applications of wood, it is necessary to prepare flame-retardant coatings that can protect wood substrates during combustion. In this study, a bio-based, intumescent, flame-retardant phytic acid–melamine polyelectrolyte (PM) was prepared using phosphorus-rich biomass phytic acid and nitrogen-rich melamine as raw materials through an ion crosslinking reaction. Subsequently, a series of bio-based, flame-retardant wood coatings were prepared by optimizing the structure of urea–formaldehyde resin with the addition of melamine, sodium lignosulfonate, and PM as a flame-retardant curing agent. Woods coated with PM-containing coatings displayed significantly improved flame-retardant performances in comparison to uncoated woods. For PM-cured woods, the measured values of total heat release and total smoke production were 91.51% and 57.80% lower, respectively, compared with those of uncoated wood. Furthermore, the fire growth index decreased by 97.32%, indicating a lower fire hazard. This increase in flame retardancy and smoke suppression performance is due to the dense expanded carbon layer formed during the combustion of the coating, which isolates oxygen and heat. In addition, the mechanical properties of the flame-retardant coatings cured with PM are similar to those cured with a commercial curing agent, NH4Cl. In addition, the prepared flame-retardant coating can also stain the wood. This study proves the excellent flame-retarding and curing effect of ammonium phytate in urea–formaldehyde resin coatings and provides a new approach for the application of bio-based flame retardants in wood coatings.

polymer science

What problem does this paper attempt to address?

This paper aims to address the flammability issue of wood during combustion by preparing a bio-based, intumescent flame retardant curing agent (PM) based on phytic acid-melamine ion crosslinking and applying it to wood coatings to enhance the flame retardancy of wood. Specifically, the main objectives of the study include:

1. **Preparation of a novel flame retardant curing agent**: Utilizing phosphorus-rich biomass phytic acid (PA) and nitrogen-rich melamine (MEL), a novel bio-based flame retardant curing agent—phytic acid-melamine polyelectrolyte (PM)—was prepared through an ion crosslinking reaction.

2. **Optimization of urea-formaldehyde resin structure**: By optimizing the structure of urea-formaldehyde resin (UF) and adding melamine, sodium lignosulfonate, and PM as flame retardant curing agents, a series of bio-based flame retardant wood coatings were prepared.

3. **Improvement of wood flame retardancy**: Studies have shown that the total heat release (THR) and total smoke production (TSP) of PM-treated wood in flame tests were reduced by 91.51% and 57.80%, respectively, and the fire growth index (FGI) decreased by 97.32%, indicating a significant enhancement in flame retardancy and smoke suppression capability.

4. **Verification of mechanical properties**: The mechanical properties of wood coatings cured with PM were comparable to those cured with commercial curing agent ammonium chloride (NH₄Cl), while also providing the function of staining the wood, thereby improving the aesthetic appeal of the material.

In summary, this study demonstrates the excellent flame retardant effect and curing action of bio-based phytic acid ammonium in urea-formaldehyde resin coatings and provides a new approach for the application of bio-based flame retardants in wood coatings.