Properties of oxidatively torrefied Chinese fir residue: Color dimension, pyrolysis kinetics, and storage behavior
Yanni Xi,Xingzhong Yuan,Mengjiao Tan,Shilin Jiang,Ziliang Wang,Zhongliang Huang,Hou Wang,Longbo Jiang,Hui Li
DOI: https://doi.org/10.1016/j.fuproc.2020.106663
IF: 8.129
2021-03-01
Fuel Processing Technology
Abstract:<p><em>Chinese fir</em> residue, as an important bioenergy, was torrefied at 240–270 °C in 0–9% O<sub>2</sub> atmosphere to improve its utilization. By using colorimetry, the good relationships between mass loss during oxidative torrefaction (<em>R</em><sup>2</sup> > 0.91), proximate analysis (<em>R</em><sup>2</sup> > 0.96), elemental analysis (<em>R</em><sup>2</sup> > 0.82) and color coordinates have been established. Based on thermogravimetric analysis, the increased O<sub>2</sub> (0–9%) in the torrefaction system significantly affected the peak temperature, peak height, T<sub>50</sub>, and R<sub>50</sub> of the torrefied samples, especially the samples torrefied at 270 °C. Flynn-Wall-Ozawa, Kissinger-Akahira-Sunose, Friedman, and Coats-Redfern methods can satisfactorily estimate the apparent activation energies of the samples. As temperature and O<sub>2</sub> concentration in the torrefaction system increased, the fragmentation of lignocellulose accelerated, and the apparent activation energy of the raw sample was estimated to decrease from 121.7–135.4 to 66.0–116.6 kJ mol<sup>−1</sup>. During the 30 days of storage, the increased hydrophobicity and composition change reduced the loss of dry matter, color change, and aldehyde/ketone emission of the torrefied sample from 7.37%, 3.6, and 16.69 μg g<sup>−1</sup> to 1.52%, 0.1, and 2.65 μg g<sup>−1</sup>, respectively. In this work, efficient ways to accelerate the properties evaluation, improve the pyrolysis behavior of <em>Chinese fir</em> residue, and simultaneously control its aldehyde/ketone formation during storage were proposed.</p>
energy & fuels,engineering, chemical,chemistry, applied