Abstract:The C=C double bonds in the main chain of hydroxyl-terminated polybutadiene (DHTPB), obtained by the degradation of polybutadiene rubber, were partially epoxided using m-chloroperoxybenzoic acid (mCPBA) as epoxidation reagent. A series of epoxided HTPBs (EHTPB) with different epoxy contents (5%, 10% and 15%) were prepared by tuning the molar ratio of mCPBA to C=C double bonds. The structures of EHTPBs were characterized by Fourier transform-infrared (FTIR), nuclear magnetic resonance (H-1-NMR) spectroscopy and gel permeation chromatography (GPC). The epoxy percent in EHTPBs from H-1-NMR spectra was in accordance with the design. In addition, a series of EHTPB-based polyurethane elastomers (EPU) were prepared by the reaction between EHTPB and 4,4'-diphenylmethane diisocyanate with 1,4-butanediol as a chain extender. Mechanical and thermal properties of the EPU samples were characterized by tensile test, differential scanning calorimetry (DSC) and thermal gravity analysis (TGA). With increased epoxy percent in EHTPB, the Young's modulus and the tensile strength of the EPU samples increased, whereas the elongation at break decreased. The sample EPU10 prepared with 10% of epoxy had the best mechanical properties with 8.82 MPa as Young's modulus, 7.83 MPa as tensile strength, and (485 +/- 23)% as elongation at break. The elasticity recovery of the EPU sample was slightly better than HTPB-based PU (EPU0). The results with TGA test showed that the thermal degradation of EPU, similar to EPU0, was divided into three stages. However, the EPU samples had better thermal stability with the initial degradation temperature at 210 degrees C, about 30 degrees C higher than that of EPU0. The DSC results showed that the glass transition temperature (T-g) of EPU gradually increased as epoxy percent was increased, though still lower than that of HTPB (FHTPB) based PUs prepared by free-radical polymerization.

Synthesis and characterization of hyperbranched thiol hardener and their curing behavior in thiol–epoxy

Preparation and Properties of Epoxided Hydroxyl-terminated Polybutadiene Based Polyurethane Elastomers

Facile Synthesis of Novel HTPBs and EHTPBs with High Cis-1,4 Content and Extremely Low Glass Transition Temperature

Modification of Unsaturated Polyester Resin by HTPB: Effect of Introducing Method of the Rubber

STUDY ON DGE-BHBTMBP/E-51/DDS CURED

Studies on Adhesion Performance of Epoxy Resin/Polymercaptan Toughened with Propoxylated Glycerin Triglycidyl Ether

Nonisothermal Reaction, Thermal Stability and Dynamic Mechanical Properties of Epoxy System with Novel Nonlinear Multifunctional Polyamine Hardener

Study on the chemical modification of epoxy/anhydride thermosets using a hydroxyl terminated hyperbranched polymer

Synthesis and Characterization of Hyperbranched Epoxy with Terminal Ally Group and Its Application of Toughen Bismaleimide

The effect of amino-terminated hyperbranched polymers on the impact resistance of epoxy resins

Mixed Hyperbranched Poly(aryl Ether Ketone) Results in High Toughness and Excellent Thermal Resistance in Epoxy Resin

Effect of Synthetic Low-Odor Thiol-Based Hardeners Containing Hydroxyl and Methyl Groups on the Curing Behavior, Thermal, and Mechanical Properties of Epoxy Resins

Synthesis, Thermal Properties and Curing Kinetics of Hyperbranched BPA/PEG Epoxy Resin

Enhancing the toughness of epoxy resin by using a novel hyperbranched benzoxazine

Hyperbranched Polyester As Additives in Filled and Unfilled Epoxy-Novolac Systems

Understanding the curing kinetics of boron-based hyperbranched polysiloxane reinforced and toughened epoxy resin by rheology

Synthesis of a novel boron‐containing hyperbranched benzoxazine and its flame‐retardant properties in copolymer with epoxy resin

Diphenolic Acid-Derived Hyperbranched Epoxy Thermosets with High Mechanical Strength and Toughness

A hydroxyl-containing hyperbranched polymer as a multi-purpose modifier for a dental epoxy

The synthesis of an epoxy-terminated hyperbranched polysiloxane toughener and its application at low temperature

Synthesis and characterization of an isocyanate-terminated hyperbranched polymer and its waterborne study