A hydroxyl-containing hyperbranched polymer as a multi-purpose modifier for a dental epoxy

An Xing,Qiannan Sun,Yan Meng,Yongyi Zhang,Xiaoyu Li,Bing Han

DOI: https://doi.org/10.1016/j.reactfunctpolym.2020.104505

2020-01-01

Abstract:Despite the high cure shrinkage, inadequate degree of cure, and toxicity, dimethacrylate dental resins have remained the dominant matrices for dental composites. Bisphenol-A free cycloaliphatic epoxy resins have lower shrinkages due to the ring-opening nature; however, its mechanical strength needs to be improved. In order to reduce cure shrinkage and toxicity simultaneously improve mechanical strength, which has long been a challenge, a hydroxyl-containing hyperbranched polymer (HBP-OH) was synthesized and used as a multi-purpose modifier for a cycloaliphatic dental epoxy system. Results show that cure shrinkage of neat dental epoxy (3.46%) is about half of that of the dimethacrylate dental resin (7.65%); HBP-OH modified epoxy further reduces shrinkage to ca. 2%. Addition of HBP-OH also reduces cytotoxicity and increases the flexural strength. Addition of 7 wt% HBP-OH increases the flexural strength of the dental epoxy from 90.8 to 109.8 MPa. In addition, effects of HBP-OH addition on the reactivity, glass transition temperature, and water uptake were also reported. Results suggest that HBP-OH shows great potentials as a multi-purpose modifier for dental epoxy resins.