Effect of Spheroidizing Annealing on the Carbide Precipitation Behavior of Cr-Mo-V-W Hot Work Die Steels

Kuicen Li,Riming Wu,Yi Xu,GeGe Huang,Yingjie Wu,Wei Li

DOI: https://doi.org/10.1007/s11665-024-09503-6

IF: 2.3

2024-05-23

Journal of Materials Engineering and Performance

Abstract:The effect of the spheroidizing annealing on the carbide precipitation behavior of Cr-Mo-V-W die steels (SR19 ® ) was systematically investigated. Thermodynamic simulation was applied for the optimization of the new spheroidizing annealing process. Microstructure was revealed by SEM and TEM. The small size precipitations (average diameter < 200 nm) obtained by quenching–tempering–holding (QTH) annealing process reached 67.27%, which is 7.22% higher than that by traditional continuous cooling holding annealing of 60.05%. It testified that the newly proposed QTH annealing process effectively improved the uniformity of precipitations as well as reduced the detrimental fresh martensite. It was determined by STEM-EDS that the larger (average diameter 200-400 nm) spherical particles were mostly Cr-rich M 23 C 6 carbides, whereas the smaller (average diameter 50-200 nm) spherical particles were mostly Mo-W-rich M 6 C carbides.

materials science, multidisciplinary