Abstract:In order to analyze the characteristics of cutting residual stress distribution at the arc‐shaped cutout of steel box girder diaphragm and to study its fatigue cracking mechanism. Taking Xia Zhang Bridge as the engineering background, this paper proposes a systematic method for calculating the residual stress field at the arc‐shaped cutout of the diaphragm. First, a mathematical model of the cutting heat source was established for predicting the temperature field changes during the cutting process of the diaphragm. Then, a 3D thermoelastic‐plastic finite element model was established using Abaqus to parametrically analysis the residual stresses during the fabrication of the transverse spacer. The results show that the cutting heat source creates a "thermal stagnation" effect at the curved notch, which leads to the local metallurgical transformation of the metal surface layer, which is unfavorable to its fatigue performance. The residual stresses are mainly concentrated near the cutting line, and the transverse residual stresses are lower at the free edge of the cutting line, which is easy to crack, and higher in the middle of the arc section of the arc notch. Inside the transverse bulkhead, at 14.5 mm from the free edge of the cut, in addition to the existence of high longitudinal residual tensile stress, its transverse residual tensile stress is also high, with a peak value of 199.3 MPa. Thermal cutting produces high residual tensile stress at the free edge, and the tensile stress cycle formed under the combined effect of wheel load is one of the reasons for the formation of initial fatigue cracks.

Fatigue damage investigation on diaphragm cutout detail on orthotropic bridge deck based on field measurement and FEM

Investigation of the Fatigue Stress of Orthotropic Steel Decks Based on an Arch Bridge with the Application of the Arlequin Method

Investigation on fatigue cracks of diaphragm cutout in bridge orthotropic steel deck

Fatigue Performance Evaluation for an Orthotropic Steel Bridge Deck Based on Field Hotspot Stress Measurements

Numerical Simulation of Fatigue Cracking of Diaphragm Notch in Orthotropic Steel Deck Model

Fatigue performance of cracked diaphragm cutouts in steel bridge reinforced employing CFRP/SMA

Stress Analysis of Fatigue Vulnerable Zones in Orthotropic Steel Bridge Decks

Analysis of Residual Stresses in Curved Cutouts of Steel Box Girder Transverse Diaphragms

Diagnosis and Mitigation of Fatigue Damage in Longitudinal Diaphragms of Cable-Stayed Bridges

Fatigue evaluation and structural optimization of rib-to-diaphragm connection in orthotropic steel decks

Fatigue behavior of typical details of orthotropic steel bridges in multiaxial stress states using traction structural stress

Fatigue Property and Improvement of a Rounded Welding Region between the Diaphragm Plate and Closed Rib of an Orthotropic Steel Bridge Deck

Fatigue Analysis of Long-Span Steel Truss Arched Bridge Part I: Experimental and Numerical Study of Orthotropic Steel Deck

Fatigue assessment of orthotropic steel bridge decks based on strain monitoring data

Fatigue behaviour of root crack in stiffener-to-deck plate weld at crossbeam of orthotropic bridge decks

Hot Spot Stress Approach For Fatigue Life Assessment In Welded Bridge Connections Using Monitoring Data And Fem Analysis

XFEM based study on fatigue performance of rib-to-diaphragm welded joints considering initial defects

A case study of fatigue cracks in orthotropic steel bridge decks

Dynamic Property Analysis of Orthotropic Bridge Deck with Local Fatigue Crack

Fatigue failure of welded details in steel bridge pylons

Fatigue Resistance Analysis of the Orthotropic Steel Deck with Arc-Shaped Stiffener