Abstract:High-temperature mechanical properties of high-boron austenitic steels (HBASs) were studied at 850 °C using a dynamic thermal-mechanical simulation testing machine. In addition, the thermal fatigue properties of the alloys were investigated using the self-restraint Uddeholm thermal fatigue test, during which the alloy specimens were cycled between room temperature and 800°C. Stereomicroscopy and scanning electron microscopy were used to study the surface cracks and cross-sectional microstructure of the alloy specimens after the thermal fatigue tests. The effects of carbon content on the mechanical properties at room temperature and high-temperature as well as thermal fatigue properties of the HBASs were also studied. The experimental results show that increasing carbon content induces changes in the microstructure and mechanical properties of the HBASs. The boride phase within the HBAS matrix exhibits a round and smooth morphology, and they are distributed in a discrete manner. The hardness of the alloys increases from 239 (0.19wt.% C) to 302 (0.29wt.% C) and 312 HV (0.37wt.% C); the tensile yield strength at 850 °C increases from 165.1 to 190.3 and 197.1 MPa; and the compressive yield strength increases from 166.1 to 167.9 and 184.4 MPa. The results of the thermal fatigue tests (performed for 300 cycles from room temperature to 800 °C) indicate that the degree of thermal fatigue of the HBAS with 0.29wt.% C (rating of 2–3) is superior to those of the alloys with 0.19wt.% (rating of 4–5) and 0.37wt.% (rating of 3–4) carbon. The main cause of this difference is the ready precipitation of M23(C,B)6-type borocarbides in the alloys with high carbon content during thermal fatigue testing. The precipitation and aggregation of borocarbide particles at the grain boundaries result in the deterioration of the thermal fatigue properties of the alloys.

Effect of Coherent Twin Boundary on the Low-Cycle Fatigue Property of 321 Austenitic Stainless Steel

Effects of low-cycle fatigue on static mechanical properties, microstructures and fracture behavior of 304 stainless steel

Variation In Mechanical Properties, Microstructures And Fracture Behavior Of 304 Stainless Steel During Low-Cycle Fatigue

The low-cycle fatigue, deformation and final fracture behaviour of an austenitic stainless steel

Effects of Grain Boundary Engineering on the Microstructure and Corrosion Fatigue Properties of 316L Austenitic Stainless Steel

Grain Boundary Engineering for Control of Fatigue Fracture in 316L Austenitic Stainless Steel

Novel role of thermomechanical grain boundary engineering in the microstructure evolution of austenitic stainless steel

Strain-Annealing Based Grain Boundary Engineering to Evaluate its Sole Implication on Intergranular Corrosion in Extra-Low Carbon Type 304L Austenitic Stainless Steel

Bending Fatigue Behavior of 316L Stainless Steel up to Very High Cycle Fatigue Regime

Deformation Mechanisms of Selective Laser Melted 316l Austenitic Stainless Steel in High Temperature Low Cycle Fatigue

Creep-fatigue interactive behavior and damage mechanism of TP321 stainless steel under hybrid-controlled conditions

Effect of Surface Modification on the High Temperature Low Cycle Fatigue Performance of LPBF 316L Austenitic Steel

Effect of twin-related boundaries distribution on carbide precipitation and intergranular corrosion behavior in nuclear-grade higher carbon austenitic stainless steel

The effect of grain boundary character distribution on the mechanical properties at different strain rates of a 316L stainless steel

Effect of Heat Treatment Process on the Optimization of Grain Boundary Character Distribution in Heavy Gage Austenitic Stainless Steel

Grain boundary engineering of AL6XN super-austenitic stainless steel: Distinctive effects of planar-slip dislocations and deformation twins

Effects of Carbon Content on High-Temperature Mechanical and Thermal Fatigue Properties of High-Boron Austenitic Steels

Effect of secondary austenite on fatigue behavior of S32750 super duplex stainless steel

Effect of crystallographic features on low-temperature fatigue ductile-to-brittle transition for simulated coarse-grained heat-affected zone of bainite steel weld

Evaluation of Grain Boundary Network and Improvement of Intergranular Cracking Resistance in 316L Stainless Steel after Grain Boundary Engineering