The Versatile Establishment of Charge Storage in Polymer Solid Electrolyte with Enhanced Charge Transfer for LiF‐Rich SEI Generation in Lithium Metal Batteries

Weizhong Liang,Xuanyi Zhou,Biao Zhang,Zishao Zhao,Xin Song,Ke Chen,Li Wang,Zengsheng Ma,Jun Liu
DOI: https://doi.org/10.1002/anie.202320149
2024-03-03
Angewandte Chemie International Edition
Abstract:In this study, a porous organic polymer with "charge storage" properties was prepared and doped into a polymer composite solid electrolyte to study the effect of sufficient charge transfer on the decomposition of lithium salts. The results show in contrast to porphyrins, the unique structure of POF allows for charge transfer between each individual porphyrin. Therefore, during TFSI- decomposition to the formation of LiF, TFSI- can obtain sufficient charge, thereby promoting the break of C-F and forming the LiF-rich SEI. Compared with single porphyrin (0.423 e-), POF provides 2.7 times more charge transfer to LiTFSI (1.147 e-). The experimental results show that Li//Li symmetric batteries equipped with PEO-POF can be operated stably for more than 2700 h at 60 °C. Even the Li//Li (45 μm) symmetric cells are stable for more than 1100 h at 0.1 mA cm-1. In addition, LiFePO4//PEO-POF//Li batteries have excellent cycling performance at 2 C (80% capacity retention after 750 cycles). Even LiFePO4//PEO-POF//Li (45 μm) cells have excellent cycling performance at 1 C (96% capacity retention after 300 cycles). Even when the PEO-base is replaced with a PEG-base and a PVDF-base, the performance of the cell is still significantly improved
chemistry, multidisciplinary
What problem does this paper attempt to address?