Catalytic Activity and Mechanical Stability of ZIFs‐Derived CoCeOx/Cordierite Monolithic Catalysts

Fan Zhang,Heng Zhang,Dongfang Wu

DOI: https://doi.org/10.1002/slct.202400175

2024-06-08

ChemistrySelect

Abstract:CoCeOx/cordierite derived from ZIFs is prepared by dipping method. The phase transition of ZIFs is first induced by the addition of excess cerium nitrate, and then tannic acid is used as a chelating agent to remove excess Ce and expose the Co active site. Finally, the complete conversion temperature of the monolithic catalyst for o‐xylene is 295 °C. Bimetallic oxide catalysts derived from zeolitic imidazolate frameworks (ZIFs) have good catalytic oxidation activity, but their application is limited because the powder is not conducive to industrial production. In this study, CoCeOx/cordierite monolithic catalysts derived from ZIFs were prepared by a simple impregnation method. Firstly, a phase transition of Co‐ZIF was induced in ethanol solution by adding excessive Ce(NO3)3. Subsequently, tannic acid (TA) was used to chelate excess metal on the surface to expose more active sites. Meanwhile, TA staying on the surface of the precursor could also prevent the accumulation of Ce at high temperatures. After the activity test, CoCeOx/cordierite showed excellent activity for the catalytic oxidation of o‐xylene with a T90 of 295 °C. The mechanical stability of the catalyst was also tested by ultrasonic vibration method. In addition, we investigated the influence of factors such as impregnation cycles and TA treatment time on the physical and chemical properties. This paper provides a new idea for preparing monolithic catalysts derived from ZIFs.

chemistry, multidisciplinary