Elucidation of Ce/Zr ratio effects on the physical properties and catalytic performance of CuOx/CeyZr1-yO2 catalysts
Mohammed Sifat,Michal Luchowski,Amol Pophali,Wenhui Jiang,Yunfan Lu,Byeongseok Kim,Gihan Kwon,Kwangsuk Yoon,Jihun Kim,Kwangjin An,Sang Eun Shim,Hocheol Song,Tae Jin Kim
DOI: https://doi.org/10.1039/d4cy01012d
IF: 6.177
2024-10-29
Catalysis Science & Technology
Abstract:Although cerium oxide (CeO2) is widely used as a catalyst support, its limited defect sites should be improved. The incorporation of zirconium (Zr) in the cerium (Ce) lattice is shown to increase the number of oxygen vacancies and improve catalytic activity. Using a fixed surface density (SD) of copper (# of Cu atoms/nm2) as a surface species, the role of the support (CeyZr1-yO2 (y = 1.0, 0.9, 0.6, 0.5, and 0.0)) and defect site effects for CO oxidation reaction were investigated. The spectroscopic (e.g., Raman, XRD) and microscopic (e.g., SEM-EDX, TEM) characterization techniques were applied to evaluate the defect sites, crystallite size, lattice parameters, and chemical composition of catalysts. CO oxidation with varied CO:O2 ratios (1:5, 1:1, and 1:0.5 (stoichiometric)) was used as a model reaction to describe the relationship between the structure and catalytic performance of each catalyst. Based on the characterization results of CeyZr1-yO2 materials, the addition of Zr causes physical and chemical changes to the overall material. The inclusion of Zr into the structure of CeO2 decreased the overall lattice parameter of the catalyst and increased the number of defect sites, while CuOx/CeyZr1-yO2 displayed lower catalytic ability compared to a CuOx/CeO2 catalyst. It was concluded that defect sites of support material were not directly linked to the increased activity of CeyZr1-yO2 supported catalysts.
chemistry, physical