Superior photodegradation efficiency of enrofloxacin by aluminum-doped Ni0.4Mn0.3Cu0.3Al0.4Fe1.6O4 (X = 0, 0.4) spinel nanoparticles synthesized via sol–gel method

Muhammed Yasar,Zahra Khan,Muhammad Ibrahim,Fozia Noreen

DOI: https://doi.org/10.1007/s11144-024-02619-9

2024-04-05

Reaction Kinetics Mechanisms and Catalysis

Abstract:Aluminum-doped Ni 0.4 Mn 0.3 Cu 0.3 Al 0.4 Fe 1.6 O 4 (X = 0.0.4) ferrite nanoparticles were synthesized via a sol–gel method, and their photocatalytic activity for the degradation of enrofloxacin was investigated. XRD confirmed the formation of a single-phase spinel structure, whereas FTIR revealed the presence of characteristic metal–oxygen bonds. The SEM images showed agglomerated nanoparticles with a porous structure, and EDX confirmed the expected elemental composition. BET) analysis revealed that Al doping significantly enhanced the surface area and pore volume of the nanoparticles. The photocatalytic performance of the synthesized nanoparticles was evaluated by studying the degradation of enrofloxacin under various conditions. The experiment employed 100 mg of the catalyst Ni 0.4 Mn 0.3 Cu 0.3 Al x Fe 2-x O 4 (where x = 0 and 0.4) at a pH of 7. A 10 ppm enrofloxacin solution was treated under 100 W bulb irradiation. The aluminum-doped sample exhibited superior photodegradation efficiency (94.69%) compared to its undoped counterpart (68.42%), which was attributed to enhanced light absorption, charge separation, and catalytic activity. Scavenger experiments suggest that hydroxyl radicals play a dominant role in the degradation process. The bandgap decreased from 2.3 to 1.9 eV upon aluminum doping, facilitating enhanced light absorption, conductivity and reduce the charge-carrier recombination. The synthesized nanoparticles demonstrated promising reusability, although a slight decrease in photocatalytic activity was observed after multiple cycles.

chemistry, physical