Controllable In situ Polymerization of 1,3‐Dioxolane via Sustained‐Release Effect for Solid‐State Lithium Metal Batteries
Sucheng Liu,Boyong Wu,Song Huang,Zitian Lin,Huiyu Song,Li Du,Zhenxing Liang,Zhiming Cui
DOI: https://doi.org/10.1002/aenm.202402848
IF: 27.8
2024-09-11
Advanced Energy Materials
Abstract:The introduced slow‐release carriers Triglycidyl isocyanurate (TGIC) play dual roles as initiator sustained‐release and network confinement. At the solution state, the electronegative O atoms in TGIC delay BF3 protonation process, extending the solidification time. After curing, the in situ formed crosslinked network suppresses the contact reaction between mobile organic components and NCM622 cathodes, forming the uniform and thin CEI layers. In situ formed poly(1,3‐dioxolane) (PDOL) electrolytes are of great interest due to the facile process and the improved interface contact. However, the practical application of in situ PDOL electrolytes is still plagued by fast solidification time (liquid state) and poor high‐voltage stability (solid state). Herein, the slow‐release carriers triglycidyl isocyanurate (TGIC), which play dual roles as initiator sustained‐release and network confinement, can tune DOL curing time and cathode/electrolyte interface chemistry is demonstrated. Specifically, the electronegative C≐O and epoxy groups in TGIC have an affinity with BF3, the decomposition product of lithium bis(oxalate)borate (LiDFOB), delaying BF3 protonation reaction and thus extending DOL solidification time. In addition, the epoxy groups in TGIC serve as crosslinking sites to form in situ crosslinked polymer electrolytes (TPDOL@FEC). The corresponding network structure suppresses the contact reaction between high‐fluidity organic components and cathodes, generating a uniform and thin cathode electrolyte interface layer. As a result, the TPDOL@FEC precursor solution can remain its liquid state even after resting 24 h at room temperature. The assembled LiNi0.6Co0.2Mn0.2O2||TPDOL@FEC||Li cells display an impressive capacity retention of 91.5% after 100 cycles at 4.4 V (0.5 C). This study is expected to be a leap in the pursuit of practically feasible in situ formed PDOL electrolytes.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,energy & fuels