A tantalum-containing zirconium-based metallic glass with superior endosseous implant relevant properties

Yunshu Wu,Feifei Wang,Yao Huang,Fu Zheng,Yuhao Zeng,Zhen Lu,Songlin Wang,Baoan Sun,Yuchun Sun

DOI: https://doi.org/10.1016/j.bioactmat.2024.04.014

IF: 18.9

2024-05-17

Bioactive Materials

Abstract:Highlights • From atomic structure, the lack of crystal phases and uniform elements distribution in amorphous Zr 58 Cu 25 Al 14 Ta 3 MG guaranteed less ion releases below the safety limit, compared with the crystalline counterpart, thus ensuring cell viability. • From surface chemistry, amorphous Zr 58 Cu 25 Al 14 Ta 3 MG enabled an extensive and direct material-cell contact with Ta, improving the reparative M2 macrophage activity, pro-angiogenic VEGF signaling pathway and pro-osteogenic BMP signaling pathway in vitro , hence achieving a better osseointegration in vivo. Zirconium-based metallic glasses (Zr-MGs) are demonstrated to exhibit high mechanical strength, low elastic modulus and excellent biocompatibility, making them promising materials for endosseous implants. Meanwhile, tantalum (Ta) is also well known for its ideal corrosion resistance and biological effects. However, the metal has an elastic modulus as high as 186 GPa which is not comparable to the natural bone (10–30 GPa), and it also has a relative high cost. Here, to fully exploit the advantages of Ta as endosseous implants, a small amount of Ta (as low as 3 at. %) was successfully added into a Zr-MG to generate an advanced functional endosseous implant, Zr 58 Cu 25 Al 14 Ta 3 MG, with superior comprehensive properties. Upon carefully dissecting the atomic structure and surface chemistry, the results show that amorphization of Ta enables the uniform distribution in material surface, leading to a significantly improved chemical stability and extensive material-cell contact regulation. Systematical analyses on the immunological, angiogenesis and osteogenesis capability of the material are carried out utilizing the next-generation sequencing, revealing that Zr 58 Cu 25 Al 14 Ta 3 MG can regulate angiogenesis through VEGF signaling pathway and osteogenesis via BMP signaling pathway. Animal experiment further confirms a sound osseointegration of Zr 58 Cu 25 Al 14 Ta 3 MG in achieving better bone-implant-contact and inducing faster peri-implant bone formation. Graphical abstract Download : Download high-res image (290KB) Download : Download full-size image

engineering, biomedical,materials science, biomaterials