Effects of Mn, Al, and Cu on Austenite Stability and Corrosion Properties of High Cr-Equivalent Steels

DOI: https://doi.org/10.1007/s11665-024-09653-7

IF: 2.3

2024-06-07

Journal of Materials Engineering and Performance

Abstract:Several Fe-based model alloys containing 15-28 wt.% Mn, 10-16 wt.% Cr, 0-5 wt.% Ni, 0-5 wt.% Al, and 0-3 wt.% Cu to obtain more economical corrosion-resistant steels were produced. The microstructural investigations showed that in the absence of Ni, even 28 wt.% of Mn failed to stabilize the austenite in the high Cr-equivalent alloys. An almost fully austenitic microstructure was developed in alloys comprising 5 wt.% Ni and 3 wt.% Cu. The potentiodynamic polarization and electrochemical impedance spectroscopy tests were performed in 3.5 wt.% NaCl solution. An alloy containing 28 wt.% Mn showed the lowest corrosion resistance ( i corr ≈ 5.4 μA/cm 2 ), possibly because of the formation of less stable Mn oxides. In a 15 wt.% Mn steel, no satisfying corrosion resistance was obtained by 10 wt.% Cr and 5 wt.% Al ( R p ≈ 27 kΩ.cm 2 ). Only 5 wt.% Ni enhanced the corrosion resistance, considerably. Alloys containing 16 wt.% Mn, 12 wt.% Cr, 3 wt.% Al, and 5 wt.% Ni with and without 3 wt. % Cu showed an R p of ~ 525 and ~ 170 kΩ.cm 2 , respectively. The Cr role was also crucial such that R p for an alloy with a similar composition and 16 wt.% Cr reached ~ 700 kΩ.cm 2 .

materials science, multidisciplinary