Abstract:Phosphogypsum (PG) is a kind of industrial solid waste with high impurity content and low utilization rate. In this study, α-hemihydrate gypsum (α-HH) was synthesized from PG in H3PO4–H2O solution (wet-process phosphoric acid solution and phosphoric acid solution) under atmospheric pressure. The crystal morphology of α-HH was controlled by adding F and Al compound regulators, and the mechanical properties of α-HH were improved. The difference of α-HH synthesized by PG with different qualities was analyzed, and the mechanism of α-HH morphology was studied by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and energy-dispersive spectroscopy (EDS). Results showed that in the wet-process phosphoric acid solution, α-HH synthesized from white PG (by H3PO4–H2SO4 two-step method) had better whiteness, purity, and mechanical properties compared with that from industrial PG, and the performance indexes of the α-HH products met the requirements of α50 grade in JC/T 2038–2010 α-high-strength gypsum in China and have a good commercial application prospect. Moreover, in the phosphoric acid solution, the average diameter of the α-HH crystal increased from 8.1 µm to 54.8 µm, the average aspect (L/D) ratio decreased from 32.65 to 0.52, and the induction period and growth period of the α-HH crystal were prolonged with the increase in regulator dosage. F− and Al3+ ions were preferred to adsorb on the crystal faces. The growth of the crystal parallel to c-axis (200), (020), and (400) was inhibited, and the morphology of the α-HH crystal changed from whisker to short column. When the dosage of the regulator was 1.1 %, the 2 h bending strength of the α-HH product was 6.56 MPa, and the drying compressive strength was 52.4 MPa. This study provides a new technique and method for the synthesis of high-strength α-HH products from PG.

A novel process approach of a circular economy practice in the production of hydroxyapatite from phosphogypsum

An Evaluation of Phosphogypsum (PG) -Derived Nanohydroxyapatite (HAP) Synthesis Methods and Waste Management as a Phosphorus Source in the Agricultural Industry

Chemical Synthesis and Characterization of Hydroxyapatite Prepared from Cypraea Annulus

Reaction parameter optimization of ammonium sulfate production from phosphogypsum

Properties, Purification, and Applications of Phosphogypsum: A Comprehensive Review Towards Circular Economy

Investigating the novel process for thorough removal of eutectic phosphate impurities from phosphogypsum

Production of Nano Hydroxyapatite and Mg-Whitlockite from Biowaste-Derived products via Continuous Flow Hydrothermal Synthesis: A Step towards Circular Economy

Acid precipitation-hydrothermal synthesis of needle-like hydroxyapatite for protein adsorption from waste phosphogypsum

Synthesis of High-Purity Hydroxyapatite and Phosphoric Acid Derived from Moroccan Natural Phosphate Rocks by Minimizing Cation Content Using Dissolution–Precipitation Technique

Synthesis of α-hemihydrate gypsum from cleaner phosphogypsum

Staged purification of phosphogypsum using pH-dependent separation process

Deep removal of phosphorus and synchronous preparation of high-strength gypsum from phosphogypsum by crystal modification in NaCl-HCl solutions

Efficient extraction of impurities from phosphogypsum during crystal regulation of α‐hemihydrate gypsum

Utilization of phosphogypsum to synthesize α-hemihydrate gypsum in H3PO4–H2O solution

Efficient removal of impurities from phosphogypsum during preparation of α-hemihydrate gypsum

Synthesis and Characterizations of Hydroxyapatite using Precursor Extracted from Chicken Egg Shell Waste

Effect of mixed cation acetate electrolyte on synthesis of α‐hemihydrate gypsum from phosphogypsum

The Development of a New Phosphogypsum-Based Construction Material: A Study of the Physicochemical, Mechanical and Thermal Characteristics

A novel and sustainable approach for biotransformation of phosphogypsum to calcium carbonate using urease producing Lysinibacillus sphaericus strain GUMP2

Hydrothermal synthesis of hydroxyapatite powders using Response Surface Methodology (RSM)

Phosphorus recovery using porous calcium silicate hydrate as seed crystal in form of hydroxyapatite