Bi@Bi 2 O 3 anchored on porous graphene prepared by solvothermal method as a high-performance anode material for potassium-ion batteries

Wenna Li,Nengshuang Gao,Hechen Li,Ruicong Sun,Qingquan Liu,Bin Huang,Quanqi Chen

DOI: https://doi.org/10.1016/j.jallcom.2023.168766

IF: 6.2

2023-01-08

Journal of Alloys and Compounds

Abstract:To enhance potassium storage performance of graphene, in situ formed electroactive bismuth nanoparticles were introduced into the porous graphene. The 2 O 3 /graphene composites, which possess the special microstructure that Bi nanoparticles are coated by Bi 2 O 3 and attached to the porous graphene, was synthesized via an environmental-friendly and simple solvothermal method combined with high-temperature sintering under inert environment using graphene oxide, BiCl 3 and ethanol as raw materials. Benefiting from the special microstructure and synergistic effect of nano-bismuth particles and graphene, 2 O 3 /graphene composites display better electrochemical performance than graphene. Between 0.01 and 3.0 V (vs K + /K), the electrode was galvanostatically discharged/charged at 100 mA g −1 and the optimal 2 O 3 /graphene composite ( 2 O 3 /G-50) has large initial charge capacity (886.4 mAh g −1 ), which is significantly larger than the theoretic capacities of Bi (385 mAh g −1 ) and graphene (279 mAh g −1 ), and after 100 cycles, the high remaining charge capacity of 466.4 mAh g −1 for 2 O 3 /G-50 was obtained. While the remaining charge capacity of graphene is only 112 mAh g −1 after 100 cycles. When electrode cycled at high current density of 800 mA g −1 , the initial charge capacities of 2 O 3 /G-50 and graphene are 294.1 and 130 mAh g −1 , respectively, and the corresponding remaining capacities are 179.1 and 67.1 mAh g −1 , respectively. The results imply that the introduction of high-capacity electroactive materials and the design of special microstructures are effective strategies to significantly improve the potassium storage performance of carbon-based anode materials for potassium-ion batteries.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering