Structure evidence of Pna2 1 phase and field-induced transition of Pna2 1 / R3c in Bi 1−x Sm x Fe 0.99 Ti 0.01 O 3 ceramics

Lu Liu,Jing Chen,Xiao Li Zhu,Xiang Ming Chen

DOI: https://doi.org/10.1063/5.0043977

IF: 4

2021-04-05

Applied Physics Letters

Abstract:In this study, the structure evidence of the <i>Pna2₁</i> phase and the field-induced transition of <i>Pna2₁/R3c</i> have been quantitatively investigated in Bi_1-xSm_xFe_0.99Ti_0.01O₃ (<i>x</i> = 0.12, 0.14, and 0.16) ceramics together with the subsequent electric field-controlled magnetism. A sequential phase transition of <i>R3c</i>-<i>Pna2₁</i>-<i>Pbnm</i> is detected by Rietveld refinement of the x-ray diffraction data. Further, the electric field-induced phase transition is investigated near the morphotropic phase boundary at <i>x</i> = 0.14, where the structure is tuned from <i>Pna2₁</i> to <i>R3c</i> with poling treatment, and this transition could become reversible with as-annealing after poling. For <i>x</i> = 0.14, the structure is tuned from <i>Pna2₁</i> to <i>R3c</i> with poling treatment, and this transition could become reversible with as-annealing after poling. The phase transition is confirmed by Rietveld refinements together with VSM measurements, providing an opportunity for electric field-controlled magnetism. The magnetoelectric coupling is enhanced, and the linear magnetoelectric coefficient <i>α</i>_ME up to 0.91 mV/Oe·cm is obtained in Bi_1-xSm_xFe_0.99Ti_0.01O₃ ceramics. More importantly, the <i>R3c</i> and <i>Pna2₁</i> structures are confirmed by selected area electron diffraction and dark-field analysis at <i>x</i> = 0.14, and the high-resolution TEM image demonstrates the coexistence of the <i>R3c</i> and <i>Pna2₁</i> structures.

physics, applied