Abstract:Understanding the formation of voids in solder joints is important for predicting the long-term reliability of solder interconnects. This paper reports experimental research on the formation of void bubbles within molten solder bumps in flip-chip connections. For flip-chip-soldered electronic components, which have small solder volume, voids can be more detrimental to reliability. A previous theory based on thermocapillary flow reveals that the direction of heating influences void formation. Using different heating profiles, 480 solder joints of flip-chip assemblies were processed. A high-lead 90Pb∕8Sn∕2Ag solder was employed in the experiments. The solder samples were microsectioned to determine the actual size or diameter of the voids. A database on sizes and locations of voids was then constructed. More defective bumps, 80%, and higher void volume were found when the solder was melted from top (flip-chip side) to bottom (test board side). The observation on cases with melting direction from bottom to top had 40% defective bumps. The results show that a single big void is near the solder bump center with a few small voids near the edge. This supports the numerical study based on the thermocapillary theory. When the melting direction was reversed, many small voids appear near the edge. Big and middle-size voids tend to stay in the middle and outer regions from top towards middle layer of the bump. This experimental finding does not completely agree with the interpretation on the formation of voids by thermocapillary theory, however, the results do show that heat flux direction plays significant role in the formation and distribution of void bubbles in molten solder.

Correlation Study On Voiding in Underfill of Large Quantity Ball Grid Array Chip Using Machine Learning

A new prediction methodology for electromigration-induced solder degradation in a WL-CSP system

Image segmentation on void regional formation in the flip-chip underfilling process by comparing YOLO and mask RCNN

Effect of Dispensing Type On Void Formation Using Convolutional Neural Network

Robust BGA Void Detection Using Multi Directional Scan Algorithms

Void region segmentation in ball grid array using u-net approach and synthetic data

Optimization of novel two-step curing method for die stack epoxy bonding to reduce voids in Ball Grid Array packages for high-density interconnect applications

Analysis of warpage and reliability of very thin profile fine pitch ball grid array

An Effective Way to Solve the Void Problem of Traditional Underfill Based on NCP Technology

Quad Flat No-Lead Package With Different Thermal Profiles And Solder Pad Finishing For Void Minimization

Experimental Study of Void Formation in High-Lead Solder Joints of Flip-Chip Assemblies

Moisture Desorption and Hygro-Vapor-Thermal Induced Interfacial Delamination in Underfilled FCBGA Package During Reflow Process

Deep Reinforcement Learning-Based Pin Map Optimization of BGA Package for EMC

Finite Element Analysis of Underfill Effect on the CBGA Package Reliability under Thermal Cycling

A Binocular Machine Vision System for Ball Grid Array Package Inspection

A Machine Vision System for Ball Grid Array Package Inspection

A Novel Coarse-Fine Method for Ball Grid Array Component Positioning and Defect Inspection.

Reference-Free Path-Walking Method for Ball Grid Array Inspection in Surface Mounting Machines.

A Line-Based-Clustering Approach for Ball Grid Array Component Inspection in Surface-Mount Technology.

A Novel End-to-End Deep Learning Framework for Chip Packaging Defect Detection

Reliability Evaluation of Board-Level Flip-Chip Package under Coupled Mechanical Compression and Thermal Cycling Test Conditions