Abstract:Vanadium oxynitride (VN x O y , x+y=1) is a metallic compound between vanadium oxides (VO, V 2 O 3 , V 2 O 5 ) and vanadium nitride (VN) which would have interesting properties and functions that potentially can be supplied for different applications. In this study, vanadium nitride and oxynitride thin films were obtained by reactive magnetron sputtering using vanadium targets, Ar as plasma carrier, and a mix of N 2 and O 2 as reactive gas. The ratio of mass flow between the two gases is maintained around O 2 :N 2 =1:20 during the process. To obtain crystalline phases of oxynitrides a post rapid thermal annealing (RTP) in Ar atmosphere at 600oC and 700oC for 5 minutes was done. The purpose of the study is to define the effect of the magnetron sputtering parameters, such as reactive gas flow rates, and annealing temperature on the composition, microstructure, and optical properties of the obtained vanadium oxynitride thin films. The characterization of obtained films includes the examination of thickness and morphology by the surface profiler and SEM; identifying crystal structures and further microstructural vibration modes of molecular polarizability by X-ray diffraction and Raman spectroscopy, respectively; evaluation of the chemical composition of films by XPS analysis; assessing of optical transmittance, reflectance, and absorbance by the UV-visible- NIR spectrometer. Experimental data reveal that the annealed films can be oxynitrides when the oxygen flow rate is below 0.25 sccm and the ratio of oxygen/nitrogen ≤1/20. The annealed vanadium oxynitride films in terms of their properties are closer to vanadium nitrides than to oxides: more metallic than semi-conductive with dark appurtenance and high optical absorbance across the spectrum between 200 and 900 nm. The optical absorbance reaches almost 90% around 300 nm and then slowly reduces to 70% at 900 nm. Thus, these films could be good optical shields. For practical usage, the deposition of O 2 :N 2 =1/20, O 2 <0.25 sccm, and 600oC annealing are recommended because of the truly low transmittance (<10%) through films.

Gas-based reduction and nitridation for synthesis of vanadium nitride: Kinetics and mechanism

Phase, microstructure evolution, and periodic density functional theory study of reduction and nitridation of V2O3 with clean ammonia gas

Mechanism and experimental study on preparation of high-quality vanadium nitride by one-step vacuum carbothermal reduction nitridation method

Synthesis of ultrafine VN particles by vanadium trioxide reduction–nitridation in a CH 4 –N 2 atmosphere: Mechanistic and experimental study

Mechanistic and experimental study of VxCy nitridation in N2 atmosphere to prepare high-quality vanadium nitride

nthesis of vanadium nitride and modulation of its catalytic performance for oxygen reduction reaction †

Kinetics and Mechanism of Redox Reaction Between N,N-Dimethylhydroxylamine and Vanadium(Ⅴ)

Hydroxylamine Derivative in Purex Process Part VIII. the Kinetics and Mechanism of the Redox Reaction of N-methylhydroxylamine and Vanadium(v)

1 Kinetic Studies on Gas-Based Reduction of 2 Vanadium Titano-Magnetite Pellet 3

Thermodynamic Study of Production of Vanadium–Nitrogen Alloy and Carbon Monoxide by Reduction and Nitriding of Vanadium Oxide

Hydrothermal synthesis of vanadium nitride and modulation of its catalytic performance for oxygen reduction reaction.

Kinetic Studies on Gas-Based Reduction of Vanadium Titano-Magnetite Pellet

Mechanism on reduction and nitridation of micrometer‐sized titania with ammonia gas

Parameter Optimization and Reaction Kinetics of the Reduction of Vanadium–Titanium Sinter by CO–CO2–H2–N2 Mixed Gases

A novel method of preparing vanadium-based precursors and their enhancement mechanism in vanadium nitride preparation

Investigations of Surface VOx Species and Their Contributions to Activities of VOx/Ti0.5Sn0.5O2 Catalysts Toward Selective Catalytic Reduction of NO by NH3

(Digital Presentation) Fabrication and Characterization for Vanadium Oxynitride Thin Films By Magnetron Sputtering

Active Vanadium(IV) Species Synthesized at Low-Temperature Facilitate Excellent Performance in Low-Temperature NOx-Catalytic Removal

Mechanistic Insights Into Electrochemical Nitrogen Reduction Reaction On Vanadium Nitride Nanoparticles

Recognizing the formation of single-atom vanadium by enthalpy and its advantage in selective catalytic reduction of nitrogen oxide