Abstract:The catalytic conversion of dinitrogen (N-2) into ammonia under ambient conditions represents one of the Holy Grails in sustainable chemistry. As a potential alternative to the Haber-Bosch process, the electrochemical reduction of N-2 to NH3 is attractive owing to its renewability and flexibility, as well as its sustainability for producing and storing value-added chemicals from the abundant feedstock of water and nitrogen on earth. However, owing to the kinetically complex and energetically challenging N-2 reduction reaction (NRR) process, NRR electrocatalysts with high catalytic activity and high selectivity are rare. In this contribution, as a proof-of-concept, we demonstrate that both the NH3 yield and faradaic efficiency (FE) under ambient conditions can be improved by modification of the hematite nanostructure surface. Introducing more oxygen vacancies to the hematite surface renders an improved performance in NRR, which leads to an average NH3 production rate of 0.46 mu g h(-1) cm(-2) and an NH3 FE of 6.04 % at -0.9 V vs. Ag/AgCl in 0.10 m KOH electrolyte. The durability of the electrochemical system was also investigated. A surprisingly high average NH3 production rate of 1.45 mu g h(-1) cm(-2) and a NH3 FE of 8.28 % were achieved after the first 1 h chronoamperometry test. This is among the highest FEs reported so far for non-precious-metal catalysts that use a polymer-electrolyte-membrane cell and is much higher than the FE of precious-metal catalysts (e.g., Ru/C) under comparable reaction conditions. However, the NH3 yield and the FE dropped to 0.29 mu g h(-1) cm(-2) and 2.74 %, respectively, after 16 h of chronoamperometry tests, which indicates poor durability of the system. Our results demonstrate the important role that the surface states of transition-metal oxides have in promoting electrocatalytic NRR under ambient conditions. This work may spur interest towards the rational design of electrocatalysts as well as electrochemical systems for NRR, with emphasis on the issue of stability.

Mechanistic Insights Into Electrochemical Nitrogen Reduction Reaction On Vanadium Nitride Nanoparticles

Theory-Guided Construction of the Unsaturated V-N<sub>2</sub> Site with Carbon Defects for Highly Selective Electrocatalytic Nitrogen Reduction

Electrochemical Nitrogen Reduction To Ammonia On Transition Metal Nitrides

Vanadium carbide with periodic anionic vacancies for effective electrocatalytic nitrogen reduction

High-Efficiency Electrosynthesis of Ammonia with High Selectivity under Ambient Conditions Enabled by VN Nanosheet Array

Quantification of Active Sites and Elucidation of the Reaction Mechanism of the Electrochemical Nitrogen Reduction Reaction on Vanadium Nitride

Recent Progress in Electrochemical Nitrogen Reduction on Transition Metal Nitrides

Electrocatalytic N 2 Reduction to NH 3 with High Faradaic Efficiency Enabled by Vanadium Phosphide Nanoparticle on V Foil

Highly Selective Electrochemical Reduction Of Dinitrogen To Ammonia At Ambient Temperature And Pressure Over Iron Oxide Catalysts

Strategic Design of VO2 encased in N-doped Carbon as an Efficient Electrocatalyst for Nitrogen Reduction Reaction at Neutral and Acidic Media

(Invited) Distributed NH3 Synthesis Via Electrochemical Reduction of N2 on Transition Metal Nitrides in a PEM Electrolyzer

Electrocatalytic N2 reduction to NH3 with high Faradaic efficiency enabled by vanadium phosphide nanoparticle on V foil

Parallelising Electrocatalytic Nitrogen Fixation Beyond Heterointerfacial Boundary

Nanomaterials for the electrochemical nitrogen reduction reaction under ambient conditions

Ruthenium/titanium Oxide Interface Promoted Electrochemical Nitrogen Reduction Reaction

Selective electrochemical nitrogen fixation to ammonia catalyzed by novel microporous vanadium phosphonate via distal pathway

Research Progress on Ni‐based Electrocatalysts for Electrochemical Reduction of Nitrogen to Ammonia

Electrocatalytic N2 Fixation over Hollow VO2 Microspheres at Ambient Conditions

Interfacial electric field triggered N2 activation for efficient electrochemical synthesis of ammonia

Repairable body-centered cubic Fe 0 anchoring on porous hollow nitrogen-doped carbon spheres with adjusting electron distribution for efficient electrocatalytic ammonia synthesis

Atomic Structure Modification for Electrochemical Nitrogen Reduction to Ammonia