Abstract:The formation of a vertically aligned carbon nanotube (VA-CNT) array in a floating catalyst process was described as a synchronous growth that resulted from the interaction of fast growth and slow growth CNTs. The array growth was characterized by the observations that straight and curved CNTs were formed during growth, and the tortuosity change of the curved CNTs and a G band Raman shift during growth. These were used to deduce that pristine stress was present in the CNTs. A model of the stresses as caused by space limitation and different growth rates was used to explain the development of a synchronous growth of the VA-CNT array. The tortuosity of the curved CNTs and Raman shift decreased and were constant after the growth of a certain length of the array, indicating that constant stresses were maintained in the growing array after the growth of this length. This indicated that an ordered CNT structure was formed and a transition from random structure to ordered structure growth had taken place in the growth. The transition was explained by a thermodynamic argument using the Onsager virial theory. Based on the vapor-liquid-solid model and bottom up growth for a single CNT, the description of a synchronous growth made possible by existent stresses gives a view that accounts for the interaction between CNTs in an array, and it can provide guidelines for a more precise control of the array structure.

Decelerating Growth of Vertically Aligned Carbon Nanotube Arrays: Kinetic Controlled or Diffusion Controlled?

Growth Deceleration of Vertically Aligned Carbon Nanotube Arrays: Catalyst Deactivation or Feedstock Diffusion Controlled?

Selective growth of semiconducting single-walled carbon nanotubes solely from carbon monoxide

Growth Process Conditions of Vertically Aligned Carbon Nanotubes Using Plasma Enhanced Chemical Vapor Deposition

Large Area Growth of Aligned CNT Arrays on Spheres: Cost Performance and Product Control

Catalyst-Free in Situ Carbon Nanotube Growth in Confined Space Via High Temperature Gradient

Rational Control on Floating Catalysts for the Growth of Carbon Nanotube Assemblies: from Vertically Aligned Carbon Nanotube Arrays to Carbon Nanotube Films

Growth Mechanism and Kinetics of Vertically Aligned Carbon Nanotube Arrays

Growth Of High-Density-Aligned And Semiconducting-Enriched Single-Walled Carbon Nanotubes: Decoupling The Conflict Between Density And Selectivity

Modulating the Diameter of Carbon Nanotubes in Array Form Via Floating Catalyst Chemical Vapor Deposition

Controlled Growth of Super-Aligned Carbon Nanotube Arrays for Spinning Continuous Unidirectional Sheets with Tunable Physical Properties

Ultralow Feeding Gas Flow Guiding Growth of Large-Scale Horizontally Aligned Single-Walled Carbon Nanotube Arrays

Growth of High-Density Horizontal SWNT Arrays by Pre-Cracking of Carbon Source

Process intensification by CO 2 for high quality carbon nanotube forest growth: Double-walled carbon nanotube convexity or single-walled carbon nanotube bowls?

A New Understanding of Carbon Nanotube Growth: Activation and Deactivation of a Catalyst

Alcohol-Assisted Rapid Growth of Vertically Aligned Carbon Nanotube Arrays

Controlling growth of aligned carbon nanotube bundles arrays with microwave plasma CVD

Rapid Growth of Well-Aligned Carbon Nanotube Arrays

Carbon fiber-promoted activation of catalyst for efficient growth of single-walled carbon nanotubes

Synchronous Growth of Vertically Aligned Carbon Nanotubes with Pristine Stress in the Heterogeneous Catalysis Process

Optimizing the growth of vertically aligned carbon nanotubes by literature mining and high-throughput experiments