Abstract:Carbon-based material-supported precious metal catalysts have important applications in fuel-cell cathode electrocatalysis due to the excellent conductivity and abundance of active sites. Here, a nitrogen-doped graphene-supported bimetallic palladium–copper composite catalyst (Pd3Cu1/N-rGO) was prepared by heat-treating the aniline monomer and graphene oxide polymer, followed by supporting palladium–copper metal particles. The change in the structure and surface state of the carbon matrix can effectively control the particle size and dispersion of alloy particles and improve the catalytic performance of the catalyst to reduce the amount of palladium. The alloy nanoparticles of the prepared Pd3Cu1/10N-rGO-800 composite catalyst material are about 1.75 nm in size and the Pd content is less than 10%, which demonstrates an excellent oxygen reduction reaction (ORR) catalytic performance with a mass-normalized current density of 2.35 times that of commercial Pt/C (20 wt % Pt), mainly a four-electron transfer process, and higher catalytic stability than commercial platinum carbon (Pt/C). Most importantly, the prepared catalyst showed better methanol tolerance and much higher stability, and Pd3Cu1/10N-rGO-800 is used as a cathode catalyst material in a zinc–air battery; it presents a higher peak power density (164.39 mW/cm2) and faster discharge performance. The N-doped graphene facilitated the dispersion of the Pd–Cu nanoparticles, effectively reduced the size of alloy particles, maximized the exposure of active sites on the surface, and improved the electrocatalytic activity of oxygen reduction. Pd–Cu nanoparticles supported on N-doped graphene will potentially offer an alternative approach to utilize non-platinum metal catalysts in electrocatalyst applications of oxygen reduction.

Scalable preparation of Pd/bacteria-rGO(CNT, Ketjen) composites for efficient oxygen reduction catalyst

One‐Pot Synthesis of a Highly Active 3‐dimensional Fe−Nx−CNTs/rGO Composite Catalyst for Oxygen Reduction

Highly Dispersed and Small-Size Pd–Cu Nanoparticles Supported on N-Doped Graphene for Oxygen Reduction Reaction Catalysts

Low-Loading Cobalt Coupled With Nitrogen-Doped Porous Graphene As Excellent Electrocatalyst For Oxygen Reduction Reaction

Facile synthesis of Rh-Pd alloy nanodendrites as highly active and durable electrocatalysts for oxygen reduction reaction.

CoNx/NiFeOx/nitrogen-doping reduced graphene oxide nanocomposite derived from layered double hydroxide precursor as an efficient bifunctional electrocatalyst for oxygen electrocatalytic reactions

Synergistic coupling of P-doped Pd4S nanoparticles with P/S-co-doped reduced graphene oxide for enhanced alkaline oxygen reduction

Etching Approach to Hybrid Structures of PtPd Nanocages and Graphene for Efficient Oxygen Reduction Reaction Catalysts

An Oxygen Reduction Catalyst Derived from a Robust Pd-reducing Bacterium

Metal‐Organic‐Framework‐derived Co Nanoparticles Embedded in P, N‐Dual‐doped Porous Carbon/rGO Catalyst for Water Splitting and Oxygen Reduction

An Advanced Nitrogen‐Doped Graphene/Cobalt‐Embedded Porous Carbon Polyhedron Hybrid for Efficient Catalysis of Oxygen Reduction and Water Splitting

Sandwich-like hierarchical porous dual-carbon catalyst with more accessible sites for boosting oxygen reduction reaction

PdCo alloys@N-doped porous carbon supported on reduced graphene oxide as a highly efficient electrocatalyst for hydrogen evolution reaction

Methanol-reduced Pd nanoparticles anchored on B,N-CDs@CNT hybrid for oxygen reduction reaction

One-pot solvothermal synthesis of reduced graphene oxide-supported uniform PtCo nanocrystals for efficient and robust electrocatalysis

Reduced graphene oxide supported palladium nanoparticles via photoassisted citrate reduction for enhanced electrocatalytic activities.

Enhancing oxygen reduction reaction performance via CNTs/graphene supported iron protoporphyrin IX: A hybrid nanoarchitecture electrocatalyst

Superior Oxygen Reduction Electrocatalysis Enabled by Integrating Hierarchical Pores, Fe3C Nanoparticles and Bamboo-Like Carbon Nanotubes

A 3D Covalent Organic Framework with In-situ Formed Pd Nanoparticles for Efficient Electrochemical Oxygen Reduction

A High-Performance Electrocatalyst For Oxygen Reduction Based On Reduced Graphene Oxide Modified With Oxide Nanoparticles, Nitrogen Dopants, And Possible Metal-N-C Sites

In situ Growth of Co3O4 Nanoparticles on Nitrogen-doped Reduced Graphene Oxide for High-Efficiency Oxygen Reduction Catalysis