Modeling Dendrite Coarsening and Remelting during Directional Solidification of Al-06wt.%Cu Alloy

Ibrahim Sari,Nashmi Alrasheedi,Mahmoud Ahmadein,Joy Djuansjah,Lakhdar Hachani,Kader Zaidat,Menghuai Wu,Abdellah Kharicha

DOI: https://doi.org/10.3390/ma17040912

IF: 3.4

2024-02-17

Materials

Abstract:Research efforts have been dedicated to predicting microstructural evolution during solidification processes. The main secondary arm spacing controls the mushy zone's permeability. The aim of the current work was to build a simple sub-grid model that describes the growth and coarsening of secondary side dendrite arms. The idea was to reduce the complexity of the curvature distribution with only two adjacent side arms in concurrence. The model was built and applied to the directional solidification of Al-06wt%Cu alloy in a Bridgman experiment. The model showed its effectiveness in predicting coarsening phenomena during the solidification of Al-06wt%Cu alloy. The results showed a rapid growth of both arms at an earlier stage of solidification, followed by the remelting of the smaller arm. In addition, the results are in good agreement with an available time-dependent expression which covers the growth and coarsening. Such model can be implemented as a sub-grid model in volume average models for the prediction of the evolution of the main secondary arms spacing during macroscopic solidification processes.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The problem that this paper attempts to solve is the coarsening and remelting phenomena of secondary dendrite arms in aluminum - copper alloy (Al - 0.6wt.%Cu) during directional solidification. Specifically, the research aims to establish a simplified sub - grid model to describe the growth and coarsening processes of secondary side - dendrite arms. This model attempts to achieve this goal by reducing the complexity of the curvature distribution and only considering two adjacent side - dendrite arms.

The main contributions of the paper are as follows:
1. **Model establishment**: A simplified sub - grid model is proposed, which can predict the coarsening and remelting phenomena of secondary dendrite arms in Al - 0.6wt.%Cu alloy during directional solidification.
2. **Experimental verification**: The effectiveness of the model is verified by comparing it with the existing time - dependent expressions. The results show that at the initial stage of solidification, the two dendrite arms grow rapidly, and then the smaller dendrite arm begins to remelt.
3. **Parameter optimization**: By simulating the dendrite arms under different initial conditions, the growth and remelting processes of the dendrite arms are studied, and the key parameters in the model, such as cooling rate and initial concentration, are optimized.

### Key equations of the model
The following key equations are used in the paper to describe the growth and coarsening processes of dendrite arms:

1. **Inverse of interface area**:
\[
S_s^{-1}=\left(S_{s0}^{-n}+Kt\right)^{\frac{1}{n}}
\]
where \(S_s\) is the specific interface area, \(S_{s0}\) is the initial specific interface area, \(K\) is the coarsening rate constant, \(t\) is the time, and \(n\) is the coarsening index.

2. **Time - dependent inverse of interface area**:
\[
S_s=(1 - f_s)^r\left(S_{s0}^{-n}+Kt\right)^{-\frac{1}{n}}
\]
where \(f_s\) is the solid fraction and \(r\) is the fitting parameter.

3. **Time evolution of dendrite arm radius**:
\[
\frac{\partial r_1}{\partial t}=\frac{D_l}{r_1}\left(c_l^*-C_0^l-\Gamma\frac{m_l}{r_1}(c_l^*-c_s^*)\right)
\]
\[
\frac{\partial r_2}{\partial t}=\frac{D_l}{r_2}\left(c_l^*-C_0^l-\Gamma\frac{m_l}{r_2}(c_l^*-c_s^*)\right)
\]
where \(r_1\) and \(r_2\) are the radii of the two dendrite arms respectively, \(D_l\) is the liquid - phase diffusion coefficient, \(c_l^*\) and \(c_s^*\) are the equilibrium concentrations of the liquid phase and the solid phase respectively, \(C_0^l\) is the initial average concentration of the liquid phase, \(\Gamma\) is the Gibbs - Thomson coefficient, and \(m_l\) is the mass of the liquid phase.

4. **Liquid - phase volume and average concentration**:
\[
V_{liq}=\pi\left(R_f^2 - r_1^2 - r_2^2\right)
\]
\[
\frac{\partial(V_{liq}C_0^l)}{\partial t}=- 2\pi r_1v_1\left(\frac{c_s^*}{\text{melt solid}}\right)-2\pi r_2v_2\left(\frac{c_s^*}{\text{melt solid}}\right)
\]

5. **Mixture concentration**:
\[
C_{mix}=\frac{V_1C_s^l+V_2