Abstract:Carbon-fiber reinforced composites are made up of three different phases. Tensile or compressive deformation in the longitudinal (fiber) orientation is controlled by the fibers, leading to a linear stress strain response which ends abruptly when the fibers fail by tensile fracture or kinking in compression. Conversely, major non-linear deformations can develop under transverse compression or in-plane shear because deformation is controlled by the polymeric matrix and the interphase.In this paper, first the V-notched rail shear test was used to research the mechanical properties of composite under in-plane shear loading, and the fracture surfaces of failed specimens were examined using scanning electron microscopy (SEM). The broken samples showed a large residual shear displacement. For [0/90](8s) cross-ply laminate V-notched beam test, the failure mode is the interactions of intralaminar and interlaminar failure. The intralaminar interfacial debonding, matrix cracking and interlaminar degradation occurs in succession. Then a representative volume element (RVE) of fiber random distribution was established, with two dominant damage mechanisms-matrix plastic deformation and interfacial debonding included in the simulation by the extended Drucker-Prager model and cohesive zone model respectively. The simulation results clearly reveal the damage process of the composites and the interactions of different damage mechanisms. It can be concluded that the in-plane shear fracture initiates as interfacial debonding and evolves as a result of interactions between interfacial debonding and matrix plastic deformation. The progressive damage process and final failure mode of in-plane shear model which are based on constitute are very consistent with the observed result under SEM of V-notched rail shear test. Also a transverse shear model was established as contrast in order to comprehensively understand the mechanical properties of composite materials under shear loading, and the progressive damage process and final failure mode of composite under transverse shear loading were researched.

Modeling test strain data reveal shear damage evolution characteristic of CFRP laminates

Concurrent Multiscale Modeling of In-Plane Micro-Damage Evaluation in Z-pinned Composite Laminates

Investigation on the Compressive Mechanical Properties of Ultra-Thick CFRP Laminates

Dynamic Behavior of CFRP-Strengthened Reinforced Concrete Beams Without Stirrups under Impact Loading

Damage and Failure Mechanisms of CFRP Due to Manufacturing Induced Wrinkling Defects

Effect of resin-rich areas on failure behavior of unidirectional CFRP under transverse pure shear

Meso/macroscale study on the shear failure of CFRP laminates considering fibre rotation

A New Three-Dimensional Progressive Damage Model for Fiber-Reinforced Polymer Laminates and Its Applications to Large Open-Hole Panels

A Combined Experimental and Computational Analysis of Failure Mechanisms in Open-Hole Cross-ply Laminates under Flexural Loading

Deformation and Fracture Mechanisms of Automated Fiber Placement Pre-Preg Laminates under Out-of-plane Tensile Loading

Failure analysis of unidirectional FRP with fiber clusters under transverse pure shear

Applying a thermodynamic-based method to reveal the failure laws of CFRP stiffened plates

Failure analysis and experimental study on bolted composite joints based on continuum damage mechanics

Microscopic Progressive Damage And Failure Analysis Of Carbon-Fiber Reinforced Composite Under Shear Loading

Characterization of progressive damage behaviour and failure mechanism of carbon fibre reinforced DP590 laminates

Micromechanical modeling for longitudinal tensile property of unidirectional CFRP considering dispersion of fiber properties

Experiments and modelling of competitive failure behaviour of CFRP stepped-lap repairs with different design parameters

A progressive damage model for carbon fiber-reinforced polymer laminates subjected to fastener pull-through failure

Multi-scale concurrent analysis for bio-inspired helicoidal CFRP laminates and experimental investigation

Experimental Data on Fracture of Open-Hole Composite Laminates Subjected to Tension Loading

Failure mode analysis and prediction model of additively manufactured continuous carbon fiber‐reinforced polylactic acid