Photocatalytic oxidation degradability of ammonia–nitrogen and Ni/Co ammonia complexes in ternary precursor wastewater by constructing MoS 2 /g-C 3 N 4 heterojunction: Performance and mechanism

Xiao Wang,Yaoguo Huang,Ruihan Zhang,Yali Zhang,Linlin Chen

DOI: https://doi.org/10.1016/j.seppur.2024.127162

IF: 8.6

2024-03-25

Separation and Purification Technology

Abstract:In this study, MoS 2 /g-C 3 N 4 heterojunction photocatalysts were fabricated in order to treat ammonia–nitrogen wastewater resulting from the production of ternary cathode material precursors used in the manufacture of lithium-ion batteries. The catalysts were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), N 2 adsorption–desorption test, UV–Vis diffuse reflectance spectra (UV–Vis DRS), Fourier-transform infrared spectroscopy (FT-IR Nicolet 6700), energy dispersive X-ray spectroscopy (EDS), and X-ray photoelectron spectroscopy (XPS). The catalytic efficiency of the catalysts on ammonia–nitrogen and Ni/Co ammonia complexes in the wastewater was investigated by varying MoS 2 doping, catalyst dose, adsorption duration, and photocatalysis duration. The results showed 2.0 g/L of MoS 2 /g-C 3 N 4 -1 wt% (photocatalyst with a content of 1 wt% MoS 2 ) has the best photocatalytic efficiency. A degradation efficiency of 87.52 % for ammonia–nitrogen, 98.34 % for nickel and 97.80 % for cobalt was reached after one hour of dark adsorption and four hours of illumination. EDS and XPS analysis revealed that Ni 2+ /Ni 3+ and Co 2+ /Co 3+ were adsorbed from the solution onto the catalyst surface, and that NH 4 + /NH 3 was converted into NO 3 − and N 2 .

engineering, chemical