Shielding Effectiveness of Textile Woven Fabric with Carbon Nanotubes Yarn

Katarzyna Grabowska,Łukasz Januszkiewicz,Ewelina Pabjańczyk-Wlazło

DOI: https://doi.org/10.1080/15440478.2024.2418347

2024-11-07

Journal of Natural Fibers

Abstract:This study explores the electromagnetic properties of flat textile products enhanced with carbon nanotube (CNT) threads used as the weft. CNT threads, fabricated via dry-spinning, were integrated into fabrics by wrapping them around steel threads to form a solenoid-like structure. To further improve electromagnetic attenuation, the CNT yarn was coated with graphene oxide and silver nanoparticles. The research assessed the impact of these modifications on the fabric's ability to attenuate alternating electromagnetic fields across a range of frequencies. Results showed enhanced attenuation at 30 MHz and 500 MHz. CNT yarn wrapped around steel threads achieved attenuation efficiencies of 18 dB at 30 MHz and 22 dB at 500 MHz, with a notable 10 dB improvement at 30 MHz over the reference. Fabrics with CNT yarn coated with graphene oxide demonstrated similar performance to the reference fabric at 500 MHz and an 8 dB increase at 30 MHz. Similarly, CNT yarn with silver nanoparticles showed comparable performance at higher frequencies but matched the reference at 30 MHz. These results indicate significant enhancement at lower frequencies, with benefits diminishing at higher. This study underscores the potential of integrating CNTs and metal nanoparticles into textiles to improve electromagnetic shielding, especially across specific frequencies. 本研究探讨了用碳纳米管(CNT)线作为纬纱增强的扁平纺织品的电磁性能. 通过干法纺丝制造的CNT线通过将其缠绕在钢丝上形成螺线管状结构而被整合到织物中. 为了进一步改善电磁衰减,CNT纱线涂覆了氧化石墨烯和银纳米粒子. 该研究评估了这些修改对织物在一定频率范围内衰减交变电磁场的能力的影响. 结果显示,在30 MHz和500 MHz时衰减增强. 缠绕在钢丝上的CNT纱线在30 MHz时的衰减效率为18 dB,在500 MHz时为22 dB,在30 MHz下比参考值有10 dB的显著提高. 具有涂覆有氧化石墨烯的CNT纱线的织物在500 MHz下表现出与参考织物相似的性能,在30 MHz下增加了8 dB. 同样,含有银纳米颗粒的CNT纱线在较高频率下表现出相当的性能,但在30 MHz下与参考值相匹配. 这些结果表明,在较低频率下效果显著,在较高频率下效果逐渐减弱. 这项研究强调了将碳纳米管和金属纳米粒子集成到纺织品中以改善电磁屏蔽的潜力,特别是在特定频率下.

materials science, textiles