Bacterial‐Cellulose‐Derived Carbon Nanofiber@MnO2 and Nitrogen‐Doped Carbon Nanofiber Electrode Materials: an Asymmetric Supercapacitor with High Energy and Power Density
Li‐Feng Chen,Zhihong Huang,Haojun Liang,Qing‐Fang Guan,Shu‐Hong Yu
DOI: https://doi.org/10.1002/adma.201204949
IF: 29.4
2013-01-01
Advanced Materials
Abstract:A new kind of high-performance asymmetric supercapacitor is designed with pyrolyzed bacterial cellulose (p-BC)-coated MnO2 as a positive electrode material and nitrogen-doped p-BC as a negative electrode material via an easy, efficient, large-scale, and green fabrication approach. The optimal asymmetric device possesses an excellent supercapacitive behavior with quite high energy and power density. Nowadays, supercapacitors have drawn extensive attention because they can instantaneously transport a higher power within a very short period than rechargeable batteries, and they possess higher energy density than conventional dielectric capacitors,1 which make them promising for applications such as backup/auxiliary power sources of electric vehicles and stand-by power systems.2-5 However, commercial supercapacitors suffer from a low energy density;2, 6 certain fields, such as load-leveling and large industrial equipment, need supercapacitors with higher energy and power density to optimize their performance.7, 8 Therefore, it is essential to improve the energy density of supercapacitors significantly to meet the pressing requirements. For a long period, a great deal of work has been done to enhance energy density by extending the operating voltage using organic electrolyte or electrode materials with large capacitances in symmetric supercapacitors.9-11 Nevertheless, organic media inevitably increase the equivalent series resistance, compared with aqueous media, leading to relatively low power density.12 Moreover, some organic media are expensive, flammable, or highly toxic.13 Various categories of redox-reaction materials, including metal oxides, conductive polymers and hybrid materials,14 have been employed as electrodes to improve the energy density dramatically. Among them, MnO2, exhibiting low cost, environmental compatibility, and high theoretical pseudo-capacitance, has attracted intense attention.15, 16 However, the low conductivity of MnO2 (10−5 − 10−6 S cm−1) results in a poor charge/discharge rate for high-power applications.17 To improve the electrical conductivity, researchers have designed composites composed of nanosized MnO2 with carbon materials, including carbon nanofoams,18, 19 carbon nanotubes,7 and graphene.20, 21 Unfortunately, carbon/MnO2-based capacitors only show ideal capacitive behavior in aqueous electrolytes, where the potential window is relatively small, and consequently deliver limited energy or power densities.22 The best way to solve this problem is to utilize the effective strategy of the asymmetric system by coupling different positive and negative electrode materials with well-separated potential windows, to obtain a high operation voltage, thus producing large energy and power densities.4, 22, 23 The key points in achieving ultrahigh energy and power densities are to design an appropriate material (especially nanostructured containing-carbon materials) as a Faradic electrode and to select a suitable capacitive electrode material (usually carbon materials).2, 6, 23 Although present carbon-containing asymmetric supercapacitors exhibit good properties,5, 6, 12, 24 the preparation processes of some relevant materials (hazardous, awkward, time-consuming, or high-cost) limit their widespread application. Thus, there is urgent demand for the development of relatively simple, cost-effective, and green approaches. Bacterial cellulose (BC), a low-cost, environmentally friendly, and abundant resource, can be produced on industrial scales via the microbial fermentation process.25, 26 Furthermore, BC pellicles (p-BC) composed of interconnected nanowires have been used to prepare macroscopic-scale carbon-nanofiber aerogels26 and transparent composites.27 Here, we construct an asymmetric supercapacitor containing a 3D p-BC nanofiber-network-coated MnO2 (p-BC@MnO2) as the positive electrode prepared by redox at room temperature, and a nitrogen-doped p-BC (p-BC/N) nanomaterial as the negative electrode, derived from p-BC and urea via a facile hydrothermal reaction under mild conditions. The optimized device can be reversibly charged/discharged at a voltage of 2.0 V in 1.0 M Na2SO4 solution, reaching a considerably high energy density of 32.91 W h kg−1 and maximum power density of 284.63 kW kg−1. Meanwhile, the supercapacitor exhibits good cycling durability with 95.4% specific capacitance retained after 2000 cycles. More importantly, the electrode materials have unique characteristics, such as low cost and easy fabrication. Because the pseudocapacitance of MnO2 dominantly determines from the surface Faradic reactions,15 it is greatly desirable to prepare MnO2 nanostructures with an ultrathin morphology. Hence, we coated the carbon nanofibers with MnO2 nanofilms, which provide a high electrochemically active surface area for redox Faradic reaction.12 The BC pellicles (Figure 1a) were employed as raw materials to fabricate a 3D nanofibrous carbon network of p-BC via annealing at 1000 °C for 2.0 h in N2. Then, the p-BC pellicles were immersed into 0.1 M KMnO4/0.1 M K2SO4 aqueous solution to obtain the product p-BC@MnO2 nanocomposites. Different amounts of MnO2 can easily coat on the p-BC only by controlling reaction time, leading to samples denoted here as p-BC@MnO2-xh (x = 0.5, 1.5, 2.0, 2.5 h). On increasing the reaction time, a significant increase of the amount of MnO2 deposited on the p-BC is observed by inductively coupled plasma-atomic emission spectrometry (ICP-AES). The mass percentages of MnO2 with dipping times of 0.5, 1.5, 2.0, and 2.5 h are 13.24 ± 0.14, 26.83 ± 0.27, 34.32 ± 0.34, and 38.56 ± 0.39 wt%, respectively. This suggests that MnO4− ions can be reduced spontaneously to MnO2 on the surface of p-BC by oxidizing the exterior carbon, based on the redox reaction: 4MnO4− + 3C + H2O → 4MnO2 + CO32− + 2HCO3− a) Photograph of the pristine material BC pellicle. b) SEM image of p-BC. c) SEM image of the p-BC@MnO2-2h (inset: photograph of the p-BC@MnO2-2h). d–g) STEM images of the p-BC@MnO2-2h with corresponding elemental mapping images of C (e), Mn (f), and O (g). This is a highly efficient green synthesis without adding any poisonous agents; moreover, it proceeds under neutral and mild conditions. Consequently, the p-BC@MnO2-2h still maintains the initial structure of the p-BC pellicle (inset in Figure 1c). The scanning electron microscopy (SEM) image of p-BC (Figure 1b) shows that the as-pyrolyzed BC pellicle has a network structure with 10−20 nm nanowires and many interconnected pores, where the void volume allows MnO4− ions to diffuse into the pellicle and be reduced to MnO2 on the surface of the nanofibers. After deposition of MnO2, the nanocomposite still maintains a 3D structure consisting of coadjacent nanowires (Figure 1c). Furthermore, there are no obvious agglomerates of MnO2 on the exterior of p-BC pellicle (Supporting Information, Figure S1). More importantly, the scanning transmission electron microscopy (STEM) and X-ray elemental mappings (Figure 1d–g) prove that the MnO2-covering p-BC was successfully fabricated by the spontaneous reduction–deposition process; meanwhile, suggest that manganese oxide nanoparticles are homogeneously distributed throughout the p-BC pellicle. Moreover, during the preparation of the STEM specimen, MnO2 nanoparticles are still incorporated on the surface of p-BC after a long-time sonication, implying the strong interaction between MnO2 nanofilm and the p-BC nanowires. From the above discussion, we can conclude that the MnO2 nanofilm was intimately connected with the p-BC nanowires and was uniformly distributed throughout the p-BC pellicles. X-ray photoelectron spectroscopy (XPS) was used to identify the presence and oxidation state of the as-synthesized MnO2 covering p-BC. The survey XPS spectrum of the p-BC@MnO2-2h confirms the coexistence of Mn, C, and O elements (Supporting Information, Figure S2a). The Mn 2p spectrum suggests the formation of manganese oxides. Meanwhile, the p-BC@MnO2-2h exhibits a peak separation value of 4.8 eV for the Mn 3s (Supporting Information, Figure S2c), indicating Mn4+ is dominant in the product.7, 28 Next, the crystal phase of MnO2 in the products was analyzed by X-ray diffraction (XRD) (see Supporting Information). The XRD pattern suggested that the p-BC@MnO2-xh consists of MnO2 (JCPDS 42-1317) and graphitized carbon.12 In addition, for the p-BC@MnO2, with the increase of dipping time of p-BC in KMnO4/K2SO4 solution, the intensity of the peak at around 37° gradually enhances due to more MnO2 loaded on the p-BC nanowires. These results were also revealed by Raman spectroscopy (Supporting Information, Figure S3b). The G-band in the first-order Raman spectra is sharper and stronger than the D-band, indicating a high graphitization of p-BC.8, 12 The relative intensity of MnO2 peaks to C peaks suggests a gradual increase of MnO2 loaded on p-BC with the prolongation of dipping time. These results also reveal that the presence of p-BC as carbon source in the redox reaction results in the formation of a MnO2 coating on the p-BC nanowires. The N2 adsorption−desorption isotherms and pore-size-distribution curves reveal the p-BC exhibits the coexistence of micropores and mesopores,8 while the sample p-BC@MnO2-2h possesses a large sum of mesopores (Supporting Information, Figure S4). Such a mesoporous structure allows fast diffusion of electrolyte ions, owing to the reduced solid-state transport length. The porous properties of these materials are summarized in Table S1 in the Supporting Information. In the following step, the capacitive performances of the p-BC@MnO2-xh composites were evaluated using a two-electrode system with a symmetric supercapacitor p-BC@MnO2-xh//p-BC@MnO2-xh in 1.0 M Na2SO4 aqueous electrolyte. To fabricate the symmetric device, the p-BC@MnO2-xh was cut into slices (1.0 × 1.0 cm) as the electrode material without using any binding agents and/or conducting additives. The CV curves of the p-BC/p-BC and the p-BC@MnO2-0.5h//p-BC@MnO2-0.5h are similar to quasi-rectangles and exhibit near mirror-image symmetry (Figure 2a), demonstrating the ideal capacitive behavior. The CV curves exhibits larger rectangles with the increase of dipping time of p-BC in KMnO4/K2SO4 aqueous solution. The galvanostatic charge/discharge curves of the p-BC@MnO2-xh//p-BC@MnO2-xh at a current density of 1.0 A g−1 (Figure 2b) are nearly linear and symmetrical without an obvious IR drop, suggesting a rapid and reversible Faradic reaction between Na+ and the ultrathin MnO2.12 The homogeneous distribution of the MnO2 is crucially important for increasing the electrochemical capacitance of the nanocomposites without increasing charge transfer or contact resistance19 Because the formed MnO2 nanofilm is on the surface of p-BC, the capacitance of p-BC@MnO2-xh//p-BC@MnO2-xh is much larger than that of p-BC//p-BC (77.76 F g−1). Prolonging the dipping time from 0.5 h to 1.5 h, then to 2.0 h leads to a significant increase of the specific capacitance (Cs) for the electrode material (at 1.0 A g−1) from 139.78 F g−1 to 213.32 F g−1, then to 254.64 F g−1, owing to the increase of the incorporating pseudocapacitive material into the 3D porous network. Moreover, the Cs slightly enhances to 256.74 F g−1 at the dipping time of 2.5 h because most of the pseudo-capacitance charge is mainly transferred at the surface or in the bulk near the surface of the electrode material.15 Hence, we plan to employ the p-BC@MnO2-2h as the positive material of our asymmetry supercapacitor. Additionally, the Cs of the p-BC@MnO2-2h is much higher than that of MnO2 nanoflowers grown on carbon-nanotube (CNT) arrays (199.0 F g−1)29 and comparable to that of MnO2 incorporated within activated graphene.24 Electrochemical properties of the materials measured using a two-electrode system in 1.0 M Na2SO4 aqueous electrolyte. a) Cyclic voltammetry (CV) curves of p-BC@MnO2 and p-BC at the scan rate of 10 mV s−1. b) Charge-discharge curves of p-BC@MnO2 and p-BC at the current density of 1.0 A g−1. c) CV curves of p-BC/N and p-BC at the scan rate of 10 mV s−1. d) Charge-discharge curves of p-BC/N and p-BC at the current densities of 1.0 A g−1. The rate capability is a key for supercapacitors;8 hence, we plotted the Cs of p-BC and p-BC@MnO2-xh at different current densities. Clearly, the rate capability shows a slight decrease with the increase of dipping time (Supporting Information, Figure S5a), because that it is more difficult for the electrolyte to access the composite with a higher content of MnO2.12 Nevertheless, the p-BC@MnO2-2h nanocomposite still presents a good rate capacity as the uniform MnO2 nanofilm plays an important role in fast electron propagation during the charge/discharge at high current densities.30 For example, its Cs maintains as high as 197.42 F g−1 at a rate of 10 A g−1, 77.53% retention of 1.0 A g−1, which is larger than that of the MnO2 nanofibers grown on graphitic hollow carbon spheres (GHCS-MnO2) (144.0 vs. 101.0 F g−1 as the current density increases from 1.0 to 10 A g−1).12 Moreover, its rate capability is comparable to that of the multiwall carbon nanotube/MnO2 (MWNT/MnO2)7 and graphene/MnO2.5 The good electrochemical performances of the p-BC@MnO2-2h can be ascribed to its unique nanostructure; the low-cost p-BC substrate with high graphitization serves as a highly conductive matrix for fast ion and electron transport, while the ultrathin MnO2 film strongly anchoring on the surface of p-BC nanowires can effectively reduce the diffusion length of electrolyte ions during the charge/discharge process and provide a large electrochemically active surface area for the fast reversible Faradic redox reactions.12, 23 Our recent research revealed that the nitrogen-doped carbon nanofibers as the electrode material of supercapacitor can increase the capacitance.8 Therefore, nitrogen-doped p-BC (p-BC/N) may be a highly promising candidate for a cathode material of an asymmetric supercapacitor. Subsequently, we used p-BC as a precursor to synthesize the p-BC/N only through a simple hydrothermal reaction. The typical p-BC/N denoted as p-BC/N-5M was synthesized by a hydrothermal reduction with 40 mg of p-BC pellicle and 40.0 mL of 5.0 M urea aqueous solution at 180 °C for 12 h. In the preparation process, the urea aqueous solution can easily permeate through the p-BC; thus, the product can be prepared via the hydrothermal reaction on a large scale. The as-prepared p-BC/N-5M still maintains a free-standing 3D pellicle (Figure 3a) with overlapped nanowires and cross-linking pores (Figure 3a). The energy filter TEM (EFTEM) revealed the p-BC/N-5M possesses network structure consisting of 10−20 nm nanowires (Figure 3b). Moreover, the elemental mapping of p-BC/N-5M demonstrated the uniform doping of nitrogen (Figure 3c,d). a) SEM image of p-BC/N-5M (inset: photograph of p-BC/N-5M). b) Typical EFTEM image of p-BC/N-5M. c,d) Corresponding elemental mapping images of C (c) and N (d). To evaluate the nitrogen functionalities of the p-BC/N-5M, XPS was carried out. The doping of nitrogen changes the number and type of surface species (Supporting Information, Figure S6a); the N 1s peak is not obvious for p-BC; however, the high-resolution one in the p-BC/N-5M can be divided into three forms of functional groups (Supporting Information, Figure S6b); namely, pyridinic (N-6, 398.1 ± 0.2 eV), pyrrolic/pyridine (N-5, 400.0 ± 0.2 eV), and quaternary nitrogen (N-Q, 401.0 ± 0.2 eV),8 indicating there are a great many nitrogen atoms. Accordingly, the low-temperature hydrothermal reaction between the p-BC and urea may be an effective method to introduce surface functionalities into carbon materials. The plentiful N-containing species (especially, N-6 and N-Q, 5.15 atom%) would serve as electrochemically active sites for improving the capacitive properties of the materials.8, 31 After doping of nitrogen, there is a decrease in the surface area and volume of micropores owing to the destruction of pore walls and micropore blocking by functional groups.32 The p-BC/N-5M still exhibits a high SBET (252.23 m2 g−1) with a large number of mesopores (Supporting Information, Figure S7). The pore parameters of this material are also summarized in Table S1 in the Supporting Information. The preserved porous network and high mesopore ratio are profitable to the transport and diffusion of electrolyte ions during the fast charge/discharge process, facilitating the high-quality performance of the supercapacitor.5 In order to demonstrate that the p-BC/N-5M is an optimal sample as a electrode material of the supercapacitor, the controlled samples, p-BC/N-yM (y denotes the molarity of urea in aqueous solution, y = 3, 4, 6), were synthesized only by adjusting the concentration of urea solution in the reaction. The electrochemical tests of the p-BC/N were also performed via a two-electrode system in 1.0 M Na2SO4 aqueous electrolyte. CV curves of p-BC/N//p-BC/N are relatively rectangular-like shapes and display near mirror-like images (Figure 2c), which suggested the supercapacitor possesses ideal capacitive behavior and a good reversibility.33 The appearance of a few humps in CV curves was owing to the redox reactions of electrochemically active functionality groups on the surface of the electrode;8 thus, it follows that the capacitive response of the p-BC/N//p-BC/N is contribution of electric double-layer capacitance (EDLC) and redox reactions. Moreover, Cs of the p-BC/N-5M calculated from galvanostatic charge/discharge curves (Figure 2d) is 173.32 F g−1, much higher than that of p-BC (only 77.70 F g−1). Previously, it was reported that the large Cs can be ascribed to proper surface functionalities, a high nitrogen level, and appropriate nitrogen species.32 Figure S5b in the Supporting Information depicts the relationship between the Cs of p-BC/N and the discharge current density. Obviously, the Cs value of the p-BC/N-5M is much larger than that of the p-BC/N-yM at the same current density; furthermore, the p-BC/N-5M possesses a good rate capability than other p-BC/N-yM (the Cs of the p-BC/N-5M is still as high as 136.68 F g−1 even at a high current density of 50 A g−1). As a result, we chose the p-BC/N-5M as the negative electrode material of the following asymmetric supercapacitor. The good electrochemical performance of the p-BC/N-5M can be attributed to the high-content of nitrogen doping and proper nitrogen species, which can improve the capacitance, electrical conductivity, and the wettability in the electrolyte.8 In addition, the interconnected pore structure and high specific-surface area of the p-BC/N-5M can increase the accessibility for electrolyte ion diffusion and transport.31, 32 We fabricated an asymmetric supercapacitor using the p-BC@MnO2-2h as the positive electrode material and the p-BC/N-5M as the negative material with 1.0 M Na2SO4 aqueous electrolyte. Referring to previous reports, the MnO2-based carbon material is electrochemically stable within a potential window of 0−1.0 V (vs. Ag/AgCl)5 and the nitrogen-doped carbon material displays a good electrochemical stability in an electrolyte of 1.0 M Na2SO4 aqueous solution within the range −1.0−0 V (vs. Ag/AgCl).5, 32 Therefore, the working voltage of the designed asymmetric device (Figure 4a, and Supporting Information, Figure S8) can extend up to 2.0 V.13, 34 The mass ratio of the positive electrode (0.6 mg) to the negative electrode (0.9 mg) was fixed close to 0.68 on the basis of charge-balance theory.23 Figure 4b shows that the device exhibits a good capacitive behavior with nearly rectangular-shaped CV curves without obvious redox peaks, even operating voltage up to 2.0 V. Moreover, the charge/discharge curve still preserves nearly symmetric at the operation voltage as high as 2.0 V (Figure 4c), suggesting that the device exhibits ideal capacitive characteristics with a rapid I−V response and small equivalent series resistance at the voltage 2.0 V. Thereby, in the subsequent research, we chose a working voltage of 2.0 V. Capacitive performances of the asymmetric supercapacitor (p-BC@MnO2-2h//p-BC/N-5M) with the p-BC@MnO2-2h as positive electrode and the p-BC/N-5M as negative electrode in 1.0 M Na2SO4 aqueous electrolyte. a) Scheme of our asymmetric supercapacitor device. b) CV curves of different operation voltages at the scan rate of 20 mV s−1. c) Galvanostatic charge−discharge curves of different operation voltages at a current density of 0.25 A g−1. d) Potential drop (Vdrop) at different discharge current densities. e) Ragone plots of the supercapacitors. f) Digital image of a red-light-emitting diode (LED) lighted by the p-BC@MnO2-2h//p-BC/N-5M device. The rectangular shape of CV curve at sweep rate as high as 400 mV s−1 is still maintained well (Supporting Information, Figure S9a); meanwhile, the charge/discharge curves at different current densities with the operation voltage of 2.0 V are almost symmetric (Supporting Information, Figure S9b), demonstrating that the asymmetric supercapacitor exhibits a desirable fast charge/discharge property.5 From the variation of IR drop (IRdrop) at different discharge-current densities (Figure 4d), we can reasonably infer the asymmetric supercapacitor has small internal resistance (IRdrop [V] = 0.01094 + I [A/g]), which favors a high discharge power delivery in practical applications. Moreover, the Ragone plots (Figure 4e) obtained from Figure S9b,c in the Supporting Information clearly shows that such a asymmetric supercapacitor shows significant enhancement in both energy density and power density compared with the p-BC@MnO2-2h//p-BC@MnO2-2h. The maximum energy density of this asymmetric device (32.91 W h kg−1) is much higher than that of the p-BC/N-5M//p-BC/N-5M and p-BC//p-BC. The value is also much larger than those of symmetrical supercapacitor and containing-carbon MnO2 nanocompound asymmetric supercapacitors (Supporting Information, Table S2). Such a high energy density of our asymmetric capacitor is mainly attributed to the large working voltage and capacitances of two electrodes.12 To show the practical application of the p-BC@MnO2-2h//p-BC/N-5M, we connected our prototype device to a red LED and successfully lighted it (Figure 4f). More importantly, the LED was on for 90 s after being charged for 44 s at 2.0 V (see Supporting Information, Movie S1). Furthermore, the asymmetric device can deliver a maximum power density of 284.63 kW kg−1, which surpasses most of the other reported MnO2-based supercapacitors.5, 12, 24 Additionally, the device exhibits a good electrochemical stability with approximately 95.4% retention of initial specific capacitance after 2000 cycles (Supporting Information, Figure S9d). The outstanding capacitive properties of the p-BC@MnO2-2h//p-BC/N-5M can be ascribed to the use of high conductivity aqueous electrolyte and two synergetic asymmetric electrodes without any binding agents; the ultrathin MnO2 coating on p-BC affords more electrochemically active surface area for fast and reversible Faradic reaction; meanwhile, the negative electrode of the p-BC/N-5M provides much faster electron transfer, resulting in the enhancement of the working voltage. In summary, we have developed a simple, scalable, cost-effective, and green approach to fabricate one binder-free asymmetric supercapacitor using bacterial-cellulose-derived carbon nanofibers loaded with MnO2 and nitrogen-doped carbon nanofibers as electrode materials, i.e., the p-BC@MnO2-2h as a positive electrode material and the p-BC/N-5M as negative electrode material. The optimal device can be reversibly charged/discharged at an operation voltage of 2.0 V in 1.0 M Na2SO4 aqueous electrolyte, delivering a high energy density of 32.91 W h kg−1 and a maximum power density of 284.63 kW kg−1, possessing a remarkable cycling stability with approcimately 95.4% capacity remaining after 2000 continuous cycles. These promising results demonstrate such a relatively easy-synthesis, low-cost, and macroscopic-scale electrode materials have great potential in the fabrication of high-class supercapacitor devices for practical applications. Supporting Information is available from the Wiley Online Library or from the author. This work is supported by National Basic Research Program of China (Grant 2010CB934700), the Ministry of Science and Technology of China (Grant 2012BAD32B05-4), the National Natural Science Foundation of China (Grants 91022032, 91227103, 21061160492), the Chinese Academy of Sciences (Grant KJZD-EW-M01-1), and Principal Investigator Award by the National Synchrotron Radiation Laboratory at University of Science and Technology of China. As a service to our authors and readers, this journal provides supporting information supplied by the authors. Such materials are peer reviewed and may be re-organized for online delivery, but are not copy-edited or typeset. Technical support issues arising from supporting information (other than missing files) should be addressed to the authors. Please note: The publisher is not responsible for the content or functionality of any supporting information supplied by the authors. Any queries (other than missing content) should be directed to the corresponding author for the article.