One-step hydrothermal synthesis of flower-like MnO2–NixCo1−x(OH)2@carbon felt positive electrodes with 3D open porous structure for high-performance asymmetric supercapacitors

Wusheng Zuo,Chao Yang,Limin Zang,Chunliu Liang,Xin Liu

DOI: https://doi.org/10.1007/s10853-020-05548-9

IF: 4.5

2020-11-12

Journal of Materials Science

Abstract:In this study, nickel–cobalt-layered double hydroxides nanosheets combined with manganese dioxide directly coated on the carbon felt (MnO2–NixCo1−x(OH)2@CF) are prepared by a facile and novel one‐step hydrothermal process with the help of potassium permanganate (KMnO4). The CF not only plays the role of 3D open porous skeleton and current collector, but also serves as the reducing agent and anchor sites to generate OH− and MnO2 coated on the surface of CF by in situ reacting with KMnO4. The morphology and electrochemical performance of the as-prepared MnO2–NixCo1−x(OH)2@CF electrodes with different feeding molar ratio of Ni–Co are investigated and the optimum feeding molar ratio of Ni–Co is confirmed to be 8:2. The resulted MnO2–Ni0.8Co0.2(OH)2@CF electrode with a 3D open porous structure contains a large number of interconnected MnO2–Ni0.8Co0.2(OH)2 nanosheets and well-defined flower-like aggregations, which exhibits a high areal specific capacitance of 1018.6 mF cm−2 at 4 mA cm−2. Furthermore, the asymmetric supercapacitor based on the MnO2–Ni0.8Co0.2(OH)2@CF as the positive electrode and activated carbon-coated CF as the negative electrode has a maximum energy density of 49.5 μWh cm−2 and remarkable cycling stability (70.2% retention after 10,000 cycles at 20 mA cm−2).Graphical abstract

materials science, multidisciplinary

What problem does this paper attempt to address?

This paper aims to solve the problems of preparation and performance optimization of high - performance asymmetric supercapacitors (ASCs) cathode materials. Specifically, through a simple one - pot hydrothermal method, the research successfully synthesized a flower - like MnO_2–NixCo1 - x(OH)_2@carbon felt (MnO_2–NixCo1 - x(OH)_2@CF) composite with a three - dimensional open porous structure as the cathode material of ASCs. The paper explored the influence of different Ni - Co molar ratios on the material morphology and electrochemical properties, and determined that the optimal Ni - Co molar ratio is 8:2. In addition, based on the optimized MnO_2–Ni0.8Co0.2(OH)_2@CF cathode material and activated carbon - coated carbon felt (AC - CF) anode material, the research also constructed ASCs and evaluated their electrochemical properties, including key indicators such as energy density, power density and cycle stability.

The main contribution of this paper lies in providing a simple and effective synthesis method that can mass - produce composites with excellent electrochemical properties, which is of great significance for the development of high - efficiency energy storage devices. The ASCs prepared by this method exhibit a high energy density (49.5 μWh/cm^2), a high power density (4.9 mW/cm^2) and good cycle stability (the capacity retention rate is 70.2% after 10,000 cycles), indicating its great potential in practical applications.