Morphological control and electrochemical performance of NiCo2O4@NiCo layered double hydroxide as an electrode for supercapacitors

Shunxiang Wang,Yongjin Zou,Fen Xu,Cuili Xiang,Hongliang Peng,Jian Zhang,Lixian Sun

DOI: https://doi.org/10.1016/j.est.2021.102862

IF: 9.4

2021-09-01

Journal of Energy Storage

Abstract:The rational tuning of the morphologies of transition metal compounds can effectively improve their electrochemical performance. In this study, NiCo2O4@NiCo-based layered double hydroxide (NiCo-LDH) composites with sheet-, grass-, and flower-like morphologies were facilely synthesized on carbon cloth by controlling the hydrothermal reaction time. The electrochemical performances of these three types of NiCo2O4@NiCo-LDHs were investigated and compared. The grass-like NiCo2O4@NiCo-LDHs (NiCo2O4@NiCo-LDH-G) exhibited a specific capacitance of 5810 mF cm−2 at 1 mA cm−2, which is higher than that of the sheet-like NiCo2O4@NiCo-LDHs (NiCo2O4@NiCo-LDH-S) (5180 mF cm−2 at 1 mA cm−2) and flower-like NiCo2O4@NiCo-LDHs (NiCo2O4@NiCo-LDH-F) (4504 mF cm−2 at 1 mA cm−2). Owing to the interconnected network structure and reduced impact of volume expansions, NiCo2O4@NiCo-LDH-G showed a better electrochemical performance than NiCo2O4@NiCo-LDH-S and NiCo2O4@NiCo-LDH-F. NiCo2O4@NiCo-LDH-G was further investigated for use as a positive electrode in an asymmetric supercapacitor (ASC). The constructed ASC exhibited a high specific energy of 81 Wh kg−1 at 0.85 kW kg−1 and an outstanding cycling stability of 88% capacitance retention after 5000 cycles, thereby demonstrating the promising application of this system in the energy storage field.

energy & fuels

What problem does this paper attempt to address?

This paper aims to address the optimization of the electrochemical performance of supercapacitor electrode materials. Specifically, the authors synthesized NiCo2O4@NiCo layered double hydroxide (NiCo-LDH) composites with three different morphologies: sheet-like, grass-like, and flower-like, by controlling the hydrothermal reaction time, and studied the effects of these different morphologies on electrochemical performance. The study shows that the grass-like NiCo2O4@NiCo-LDH (NiCo2O4@NiCo-LDH-G) exhibits the highest specific capacitance (5810 mF cm² at 1 mA cm²), outperforming the sheet-like and flower-like structures. Additionally, this material also demonstrates good cycling stability and high energy density, making it a promising candidate for asymmetric supercapacitors.

### Main Issues and Solutions:
1. **Improving Electrochemical Performance**:
- **Method**: Synthesize NiCo2O4@NiCo-LDH composites with different morphologies by controlling the hydrothermal reaction time.
- **Result**: The grass-like structure of NiCo2O4@NiCo-LDH-G exhibits the highest specific capacitance and the best electrochemical performance.

2. **Enhancing Cycling Stability**:
- **Method**: Utilize the high surface area and interconnected network structure of the grass-like morphology to reduce the impact of volume expansion.
- **Result**: NiCo2O4@NiCo-LDH-G retains 88% of its capacity after 5000 cycles.

3. **Increasing Energy Density**:
- **Method**: Construct an asymmetric supercapacitor (ASC) using NiCo2O4@NiCo-LDH-G as the positive electrode material and activated carbon (AC) as the negative electrode material.
- **Result**: The ASC device achieves a high energy density of 81 Wh kg⁻¹ at a power density of 0.85 kW kg⁻¹.

### Conclusion:
By controlling the hydrothermal reaction time, the morphology of NiCo2O4@NiCo-LDH can be effectively regulated, significantly enhancing its electrochemical performance. The grass-like structure of NiCo2O4@NiCo-LDH-G exhibits superior performance in terms of specific capacitance, cycling stability, and energy density, making it an ideal electrode material for high-performance supercapacitors.