Abstract:Ceramic coatings with aluminum titanuate (Al2TiO5) were prepared on Ti–6Al–4V alloy using pulsed bi-polar Micro-arc Oxidation (MAO). The micromorphology and phase composition of the micro-arc-oxidition ceramic coatings on the titanium alloy were characterized by X-ray powder diffraction (XRD), and scanning electron microscopy (SEM) respectively. The results revealed that the distinct discharge channels and pores on the surface of the micro-arc-oxidition coatings appeared, and these channels were connected in the molten state. The electrolyte concentration was inversely proportional to the coating hardness; additionally, the coating prepared with sodium aluminate and sodium hypophosphite concentrations of 4 g/L and 0.5 g/L, respectively, was the most refined after high-temperature sintering, and it was demonstrated to better prevent oxidation. Increasing the electrolyte concentration coincided with fluctuating coating thermal shock resistance. The thermal shock resistance of the coating respectively prepared with sodium aluminate, and the sodium hypophosphite concentrations of 4 g/L and 0.5 g/L was the highest. Additionally, the high-concentration coatings performed significantly better than the low-concentration coatings. The oxidation resistance of the coating samples was also significantly higher than that of the TC4 titanium alloy substrate. The adhesion strength between the coatings and the substrate with and without the sealing treatment was measured by tensile tests. Then, the high-temperature oxidation performance of the coating samples with and without the sealing treatment was investigated by conducting a high-temperature oxidation experiment at a calcinating temperature of 500 °C. The results indicate that the adhesion strength between the coatings and substrate was high for the as-prepared and sealed micro-arc oxidation samples regardless of whether they were calcined. The high-temperature oxidation mass increase curves for the sealed and unsealed coating samples calcined at 500 °C for 500 h revealed that the high-temperature-oxidation-induced mass increase of the coating samples sealed with a sodium silicate solution was much lower than that of the titanium alloy substrate. Thus, the sealing treatment significantly improved the high-temperature oxidation resistance of the TC4 titanium alloy. Lastly, the high-temperature oxidation behavior at 500 °C was analyzed and discussed.

Improvement of the tribological and high‐temperature oxidation behavior of mild steel by alumina coating

Improved wear and corrosion resistance of alumina alloy by MAO and PECVD

Improving the Wear Resistance Properties of 7A04 Aluminum Alloy with Three Surface Modification Coatings

Effect of Treatment with Microarc Oxidation Technology on Tribological Properties of Nonvalve Metal Low-Carbon Steel

Improvement of tribological performance by micro-arc oxidation treatment on selective laser melting Ti6Al4V alloy

Tribological study of W-S-(C) sputtered coatings sliding against aluminium at elevated temperatures

Microstructure and Corrosion Study on Friction Surfaced Aluminum Alloy Coatings over Mild Steel

Improvement of the Tribological Properties of Alumina Coatings by Zirconia Addition

Performance Study of MCrAlY Flame Sprayed Coating on AISI 304 Stainless Steel of Microstructure and Sliding Wear at High Temperatures

Wear and corrosion resistance of Al2O3 and TiC deposition on steel substrate using Self- propagating High temperature Synthesis method

Effect of Current Density on the Wear Resistance of Ceramic Coatings Formed on 7075 Aluminum Alloy via Microarc Oxidation

Tribological behavior of novel Al2O3-La2O3 HVOF composite coatings

Wear Behaviour of Friction Surfaced Al-Ni and Al-SiC Coatings over Mild Steel

Effects of nanoceramic particle size and content on the wear resistance of micro-arc oxidation coatings for 2A12 aluminum alloy

High-temperature oxidation resistance of ceramic coatings on titanium alloy by micro-arc oxidation in aluminate solution

Tribological behaviour of TiAlN and AlCrN coatings on stainless steel

Improving the mechanical and tribological properties of TiAlSiN coatings by annealing

Enhanced Resistance of Ti6Al4V Alloy to High-Temperature Oxidation and Corrosion by Forming Alumina Composite Coating

Parameter optimization for enhancing tribological properties of sol–gel alumina and aluminum silicate-coated aluminum alloy: Grey–Taguchi method

Tribological and corrosive degradation of differently surface engineered 17-4 PH steel

Microstructure and dry sliding wear evaluation of functionally graded coating deposited via atmospheric plasma spray