XRD and 29Si MAS NMR study on carbonated cement paste under accelerated carbonation using different concentration of CO2
Wei Liu,Yong-Qiang Li,Lu-Ping Tang,Zhi-Jun Dong
DOI: https://doi.org/10.1016/j.mtcomm.2019.05.007
IF: 3.8
2019-06-01
Materials Today Communications
Abstract:<p>In this study, the chemical composition of cement pastes, exposed to accelerated carbonation using different concentration of CO<sub>2</sub> (3%, 10%, 20%, 50%,100%), have been determined and compared with those of natural carbonation (0.03%). Quantitative X-ray diffraction (QXRD) and <sup>29</sup>Si Magic Angle Spinning Nuclear Magnetic Resonance (MAS NMR) were used for characterisation and quantitative analysis of the carbonated phases. The obtained QXRD results revealed that the complete carbonation was hardly attained. Calcite, aragonite and vaterite were in co-existence after accelerated carbonation, while vaterite was dominant. The preferential polymorphic precipitation of the three crystal forms of calcium carbonate was affected by the carbonation degree of C-S-H and the duration of the carbonation process, but not by the concentration of CO<sub>2</sub>. The NMR results indicated that C-S-H gel was strongly decalcified, and calcium modified silica gel was formed after carbonation. The C-S-H decalcification, under all the accelerated carbonation conditions, was clearly more pronounced than that under the natural carbonation conditions. When the concentration of CO<sub>2</sub> was in the range of 3% to 20%, the ratio of decalcified to remaining C-S-H was similar, in a range of 5 to 6, while under the higher concentration of CO<sub>2</sub> this ratio was increased to >8. Therefore, in consideration of both acceleration rate and measurement uncertainty, the higher concentration, up to 20%, of CO<sub>2</sub> in an accelerated carbonation should be applicable.</p>
materials science, multidisciplinary