Instant CO2 curing for dry-mix pressed cement pastes: Consideration of CO2 concentrations coupled with further water curing

Xuemiao Li,Tung-Chai Ling

DOI: https://doi.org/10.1016/j.jcou.2020.02.012

IF: 7.7

2020-05-01

Journal of CO2 Utilization

Abstract:<p>Early-age carbonation can make a significant difference in the formation of hydration products in cement-based materials and alter the microstructural and mechanical performances. To understand in detail the impacts and their contribution to cement hydration, dry-mix cement pastes were exposed to instant carbonation with 0.04 %, 1%, 3%, 10 %, 20 % CO₂ concentrations for 2 h prior to further water curing. By increasing the CO₂ concentration, an increment in strength gain of samples at 2 h (right after early carbonation) as well as being prolonged by water curing at 1, 3, 7 days was noticed. This agrees with TGA and XRD results, demonstrating that the increases in CO₂ concentration resulted in a higher carbonation reaction and hydration degree. ²⁹Si NMR results also indicate that the higher the CO₂ concentration the lower the calcium to silica ratio (Ca/Si); thus, there is a higher degree of polymerization to promote early hydration. It can be concluded that early carbonation of 2 h in particular with a high CO₂ concentration can be beneficial for further cement hydration due to the consumption of calcium hydroxide (CH) and nuclei site effect of calcite crystals, resulting in better microstructural properties and mechanical performance.</p>

engineering, chemical,chemistry, multidisciplinary