Bright cyan-to-green color-tunable emissions from Ce3+/Tb3+ co-activated garnet phosphors for high-color-quality solid-state lighting
Liangling Sun,Jia Liang,Shaoying Wang,Qi Sun,Balaji Devakumar,Xiaoyong Huang
DOI: https://doi.org/10.1016/j.mtener.2020.100487
IF: 9.257
2020-09-01
Materials Today Energy
Abstract:<p>High-efficiency near-UV excitable inorganic phosphors with tunable emissions are highly demanded for white light-emitting diodes (LEDs) and displays. In this paper, a series of color-tunable cyan-green-emitting Ca<sub>2</sub>Lu<sub>0.99-<em>x</em></sub>Zr<sub>2</sub>(AlO<sub>4</sub>)<sub>3</sub>:1%Ce<sup>3+</sup>,<em>x</em>Tb<sup>3+</sup> (CLZA:1%Ce<sup>3+</sup>,<em>x</em>Tb<sup>3+</sup>) phosphors was synthesized via a high-temperature solid-state reaction method. Their crystal structure, morphology, emission and excitation spectra, energy transfer properties, CIE color coordinates, internal quantum efficiency and temperature-dependent spectra were systematically researched. Impressively, these CLZA:1%Ce<sup>3+</sup>,<em>x</em>Tb<sup>3+</sup> phosphors showed an intense excitation band in the 370-475 nm wavelength range with a peak at 408 nm corresponding to the 4<em>f</em>→5<em>d</em> transitions of Ce<sup>3+</sup> ions. Owing to the energy transfer from Ce<sup>3+</sup> to Tb<sup>3+</sup> ions, bright cyan-to-green color-tunable emissions were obtained in CLZA:1%Ce<sup>3+</sup>,<em>x</em>Tb<sup>3+</sup> phosphors with an increase of the Tb<sup>3+</sup> doping concentration, and the corresponding CIE color coordinates changed from (0.156, 0.249) to (0.341, 0.533) when the Tb<sup>3+</sup> doping concentration increased from <em>x</em> = 0 to 90%. The internal quantum efficiency reached up to 69%. Moreover, temperature-dependent spectra demonstrated good thermal stability and color stability of the as-prepared Ce<sup>3+</sup>/Tb<sup>3+</sup> doped Ca<sub>2</sub>LuZr<sub>2</sub>(AlO<sub>4</sub>)<sub>3</sub> phosphors. In addition, a white LED device was fabricated by coating the blend of the as-prepared cyan-emitting CLZA:1%Ce<sup>3+</sup>,10%Tb<sup>3+</sup> phosphor and commercial red phosphor CaAlSiN<sub>3</sub>:Eu<sup>2+</sup> on a 400 nm LED chip, which exhibited bright warm-white light with CIE coordinates of (0.425, 0.376), low correlated color temperature of 2975 K and high color rendering index value of Ra = 83 and R9 = 89. These results revealed that the CLZA:Ce<sup>3+</sup>,Tb<sup>3+</sup> phosphors could be excellent candidates for the application of near-UV-excited warm-white LEDs.</p>
materials science, multidisciplinary,chemistry, physical,energy & fuels