Abstract:Herein, a novel and facile electrophoretic/electrochemical deposition (EPD/ECD) method is reported for the fabrication of binder-free high-performance Fe3O4/functionalized g-C3N4 nanocomposite. In this method, through a simple EPD/ECD procedure, Fe3O4 nanoparticles are in situ simultaneously synthesized onto the edge-functionalized g-C3N4 (ef-g-C3N4) sheets electrophoretically deposited onto Ni foam. For comparison, pristine Fe3O4 nanoparticles and ef-g-C3N4 are deposited onto Ni foam via EPD and ECD procedures, respectively. The prepared materials are fully analyzed through XRD, TGA, FT-IR, Raman, FE-SEM, TEM as well as BET/BJH techniques. These analyses results verified co-deposition of fine Fe3O4 particles along with porous ef-g-C3N4 sheets onto the Ni-foam cathode, and formation of Fe3O4@ef-g-C3N4@Ni foam hybrid electrode. The formation mechanism of Fe3O4/ef-g-C3N4 nanocomposite through EPD/ECD was proposed and described in details. The electrochemical behaviors of the prepared electrodes were investigated as a binder-free supercapacitor electrodes. The results charge-discharge tests revealed that Fe3O4@ef-g-C3N4/NF is capable to deliver specific capacitance of 197.2 mA h g−1 at 0.5 A g−1 and cycle life of 96.1 % and 88.5 % after 4000 continuous cycling at current densities of 0.5 and 3 A g−1, respectively, whereas the pristine Fe3O4/NF delivered only specific capacitance of 76.9 m g−1 at 0.5 A g−1 and cycling stability of 87.6 % and 60.8 % at the similar conditions. These findings proved surprising positive synergistic contribution between Fe3O4 and edge-functionalized g-C3N4 to present high supercapacitive ability.

Solution combustion synthesized spongy structure nanopowders to promote ion diffusion in supercapacitor electrode

Facilely synthesized porous NiCo2O4 flowerlike nanostructure for high-rate supercapacitors

Nitrogen-functionalized Microporous Carbon Nanoparticles for High Performance Supercapacitor Electrode

Synthesis of NiMn-LDH Nanosheet@Ni 3 S 2 Nanorod Hybrid Structures for Supercapacitor Electrode Materials with Ultrahigh Specific Capacitance

One-step Large Scale Combustion Synthesis Mesoporous MnO2/MnCo2O4 Composite As Electrode Material for High-Performance Supercapacitors

Synthesis of Multiporous Carbon Nanofibers and Their Application in Supercapacitors

Nitrogen and Sulfur Codoped Porous Carbon Microsphere: a High Performance Electrode in Supercapacitor

Ordered Mesoporous Nickel Cobaltite Spinel with Ultra-High Supercapacitance

Green one-pot synthesis of binder-free porous edge-functionalized graphitic carbon nitride/iron oxide nanoparticles nanocomposite as an outstanding electrode for supercapacitors

Preparation of sodium lignosulfonate-based porous carbon and its application to supercapacitors

Thiocyanogen-modulated N, S Co-doped lignin hierarchical porous carbons for high-performance aqueous supercapacitors

Facile synthesis of chitosan derived heteroatoms-doped hierarchical porous carbon for supercapacitors

Synthesis of Porous Ag2S-NiCo2S4 Hollow Architecture As Effective Electrode Material with High Capacitive Performances.

Synthesis of oxygen‐deficient WO3‐x nanoplates and hollow microspheres decorated on carbon cloth for supercapacitor

Scalable combustion synthesis of graphene-welded activated carbon for high-performance supercapacitors

N/O Co-doped Porous Carbon with Controllable Porosity Synthesized via an All-in-One Step Method for a High-Rate-Performance Supercapacitor

Synthesis of biomass-based porous graphitic carbon combining chemical treatment and hydrothermal carbonization as promising electrode materials for supercapacitors

Microzone-explosion synthesis of porous carbon electrodes for advanced aqueous solid-state supercapacitors with a high-voltage gel electrolyte

Facile synthesis of CoNi2S4 nanoparticles grown on carbon fiber cloth for supercapacitor application

Ethanol-assisted Solvothermal Synthesis of Porous Nanostructured Cobalt Oxides (coo/co3o4) for High-Performance Supercapacitors

Facile fabrication 1D/2D/3D Co3O4 nanostructure in hydrothermal synthesis for enhanced supercapacitor performance