Abstract:Fiber-reinforced polymers (FRPs) are increasingly being used as substitutes for traditional metallic materials across various industries due to their exceptional strength-to-weight ratio. However, their orthotropic properties make them prone to multiple forms of damage, posing significant challenges in their design and application. During the design process, FRPs are subjected to various loading conditions to study their microscopic damage behavior, typically assessed through scanning electron microscopy (SEM). While SEM provides detailed insights into fracture surfaces, the manual analysis of these images is labor-intensive, time-consuming, and subject to variability based on the observer's expertise. To address these limitations, this research proposes a deep learning-based approach for the autonomous microscopic damage assessment of FRPs. Several computationally efficient pre-trained deep learning models, such as DenseNet121, NasNet Mobile, EfficientNet, and MobileNet, were evaluated for their performance in identifying different damage modes autonomously, thus reducing the need for manual interpretation. SEM images of FRPs with five distinct failure modes were used to validate the proposed method. These failure modes include three fiber-based failures such as fiber breakage, fiber pullout, and mixed-mode failure, and two matrix-based failures such as matrix brittle failure and matrix ductile failure. The entire dataset is divided into train, validation, and test sets. Deep learning models were established by training on train and validation sets for five failure modes, while the test set was used as the unseen data to validate the models. The models were assessed using various evaluation metrics on an unseen test dataset. Results indicate that the EfficientNet model achieved the highest accuracy of 97.75% in classifying the failure modes. The findings demonstrate the effectiveness of employing deep learning techniques for microscopic damage assessment, offering a more efficient, consistent, and scalable solution compared to traditional manual analysis.

Machine Learning-Based Damage Predicion Method for the Micro/Nano Structures Fabricated by Helium Focused Ion Beam

Helium focused ion beam induced subsurface damage on Si and SiC substrates: experiments and generative deep neural network modeling via position-dependent input

Detection and Quantification of Damage in Metallic Structures by Laser-Generated Ultrasonics

Generalized damage profile function for subsurface damage in SiC induced by helium focused ion beam under line scanning at different energies and doses

Prediction of Fatigue Crack Damage Using In-Situ Scanning Electron Microscopy and Machine Learning

Study of damage generation induced by focused helium ion beam in silicon

A Deep Learning Method for Damage Prognostics of Fiber-Reinforced Composite Laminates Using Acoustic Emission

Focused-helium-ion-beam blow forming of nanostructures: radiation damage and nanofabrication

Detecting Irradiation Defects in Materials: A Machine Learning Approach to Analyze Helium Bubble Images

Damage Quantification Method for Aircraft Structures Based on Multitask CNN-LSTM and Transfer Learning

Machine learning-based prediction for time series damage evolution of Ni-based superalloy microstructures

Analysis of Damage Induced by FIB Irradiation in Microprocess

Automatic Air-Coupled Ultrasound Detection of Impact Damages in Fiber-Reinforced Composites Based on One-Dimension Deep Learning Models

Deep Learning-Based Microscopic Damage Assessment of Fiber-Reinforced Polymer Composites

Chemomechanical damage prediction from phase-field simulation video sequences using a deep-learning-based methodology

Hydrodynamics and solid mechanics structural analysis of mold deformation in nanoimprint lithography

Prediction of microstructural-dependent mechanical properties, progressive damage, and stress distribution from X-ray computed tomography scans using a deep learning workflow

Predicting failure characteristics of structural materials via deep learning based on nondestructive void topology

Review on FIB-induced damage in diamond materials

Damage prediction of stiffened plates subjected to underwater contact explosion using the machine learning-based method

Accelerating Hydrodynamic Fabrication of Microstructures using Deep Neural Networks