Abstract:In this study, the effect of the mechanical stability of residual austenite in a carburizing layer on the wear performance was explored. First, different amounts of residual austenite were obtained by quenching and cooling 23CrNi3MoA steel after carburization. The effects of the volume fraction, size, and distribution of the residual austenite on the stability and wear performance were investigated. Second, scanning electron microscopy (SEM), transmission electron microscopy (TEM), focused ion beam (FIB), and electron backscatter diffraction (EBSD) analyses were used to characterize the severely deformed layer under friction. In addition, the impacts of the size, morphology, content, and distribution of residual austenite on the wear performance were analyzed. The final results indicated that as the k of the residual austenite decreased, the wear performance of the sample first increased and then decreased. The wear performance improved due to the reduced stability of the residual austenite, which facilitated phase transformation of the residual austenite under friction. The phase transformation of residual austenite into martensite increased the hardness of the wear surface layer. In addition, nanotwinned martensite formed in the severe wear deformation layer. The generation of nanotwins could effectively hinder dislocation movement and store high-density dislocations near the twin boundaries, thereby improving the strength of the wear layer and reducing the wear rate. However, when the residual austenite stability continued to decrease, a large amount of block-like austenite at the grain boundaries underwent excessive plastic deformation during friction. This excessive plastic deformation increased the number of dislocations and led to incoordination between the phase-transformed martensite and the original martensite during deformation. Therefore, crack nucleation increased, and crack propagation accelerated, directly increasing the amount of wear on the wear surface and decreasing the overall wear resistance of the material. In this article, the wear mechanism of residual austenite during dry sliding friction was elucidated, and a basis for reasonable control of residual austenite in production work was provided.

Effect of Short-Term Low-Temperature Austempering on the Microstructure and Abrasive Wear of Medium-Carbon Low-Alloy Steel

Sliding wear of medium-carbon bainitic/martensitic/austenitic steel treated by short-term low-temperature austempering

Effect of Austempering Temperature on Microstructure Evolution, Mechanical Properties and Wear Resistance of Carbon-free Nano-bainite Steel

Effect of Austempering below and above Ms on the Microstructure and Wear Performance of a Low-Carbon Bainitic Steel

Comparison of wear performance of bainitic and martensitic structure with similar fracture toughness and hardness at different wear conditions

A study of the abrasive wear of carbon steels

Wear Resistance of Medium Carbon Steel with Different Microstructures

Analyzing the effect of the mechanical stability of residual austenite on the wear performance

Effect of Austempering Treatment on Microstructure and Mechanical Properties of M50NiL Bearing Steel

The Strengthening Role of Cryogenic Treatment in the Mechanical Properties and Abrasive Wear of Low Alloy Wear-Resistant Steel

EFFECTS OF CRYOGENIC TREATMENT ON MICROSTRUCTURE AND WEAR RESISTANCE OF Fe-0.35C-6.3Cr MARTENSITIC STEEL

Effect of prior austenite grain size on the abrasive wear resistance of ultra-high strength martensitic steels

Abrasive Wear of High-Carbon Low-Alloyed Austenite Steel: Microhardness, Microstructure and X-ray Characteristics of Worn Surface

Microstructure and Mechanical Properties of Low- and Medium-Carbon Si-Rich Low-Alloy Steels Processed by Austemping after Intercritical Annealing

Microstructure Evolution and Mechanical Properties during Long-term Tempering of a Low Carbon Martensitic Stainless Bearing Steel

Effect of austempering temperature on microstructure and cyclic deformation behaviour of multiphase low-carbon steel

Effects of austempering on the microstructure and mechanical properties of high-strength nanostructured bainitic steel containing 3.5 wt% aluminum

Effect of Heat Treatment Parameters on the Modification of Nano Residual Austenite of Low-Carbon Medium-Chromium Steel

The influence of austenitizing temperature on prior austenite grain size and resistance to abrasion wear of selected low-alloy boron steel

Effect of Spheroidizing Annealing Process on Microstructure and Properties of Quenching and Tempering 60Cr16MoMA Martensitic Stainless Steel

The fatigue properties, microstructural evolution and crack behaviors of low-carbon carbide-free bainitic steel during low-cycle fatigue