Preparation and application of Ag-CuFe2O4 semiconductors rich in oxygen vacancies

Keren Shi,Yuren Luo,Guangyan Qian,Jiayu Luo,Mingming Li,Yuxiang Xiang,Huiqin Yao

DOI: https://doi.org/10.1016/j.surfin.2023.103485

IF: 6.2

2023-11-01

Surfaces and Interfaces

Abstract:Ag metal particles were introduced into spinel CuFe2O4, while propanetriol solution was used to increase the oxygen vacancies (OVs) concentration of the material. 1% Ag-CuFe2O4, 3% Ag-CuFe2O4, and 1% Ag-CuFe2O4-OVs were prepared by gel-sol method. These materials were characterized and tested, and the results showed that Ag particles were successfully introduced into CuFe2O4, and the oxygen vacancy concentration was significantly enhanced. Among them, 3% Ag-CuFe2O4 and 1% Ag-CuFe2O4-OVs achieved the best results in all aspects of the performance tests. The degradation rates of 91.81% and 99.31% were achieved after 180 min in 30 mg/L indole solution at pH 7.0 using 30 mg of catalyst. The effects of catalyst dosage and initial concentration of the solution on the catalytic effect were investigated by selecting a 1% Ag-CuFe2O4-OVs catalyst. Among them, the highest degradation efficiency was achieved at a catalyst dosage of 40 mg, but the degradation efficiency gradually weakened with the increase in catalyst dosage. The catalytic effect decreased to 89.13% after 5 cycles of experiments using a 30 mg catalyst, which proved that the catalyst had good reusability.

chemistry, physical,physics, applied, condensed matter,materials science, coatings & films