Abstract:Silicon is a promising negative electrode material for high‐energy‐density Li‐ion batteries (LiBs) but suffers from significant degradation due to the mechanical stress induced by lithiation. Volume expansion and lithiation in Si are strongly anisotropic but associated early interfacial transformations linked to these phenomena and their implications for electrode performance remain poorly understood. Here we develop a novel correlative electrochemical multi‐microscopy approach to study local interfacial degradation at the early stages for three different surface orientations of Si single crystals: Si(1 0 0), Si(1 1 0) and Si(3 1 1), after Li‐ion electrochemical cycling. The experimental strategy combines scanning electrochemical cell microscopy (SECCM) measurements with subsequently recorded scanning transmission electron microscopy images of high‐quality cross sections of Si electrodes, extracted at selected SECCM regions, using a novel Xe+ plasma‐focused ion beam procedure. These studies reveal significant surface orientation–dependent nanoscale degradation mechanisms that strongly control electrode performance. Si(1 0 0) was immune to interfacial degradation showing the best lithiation reversibility, whereas local nanoscale delamination was observed in Si(1 1 0) leading to a lower Coulombic efficiency. Continuous electrochemical deactivation of Si(3 1 1) was associated with delamination across the whole interface, Li trapping and formation of thick (ca. 60 nm) SiO2 structures. These results demonstrate surface crystallography to be a critical factor when designing Si‐based battery materials and strongly suggest that promoting Si(1 0 0) facets could potentially provide longer cycling life and performance due to a higher resistance to degradation.

Lithiation of silicon via lithium Zintl-defect complexes

In Situ Atomic-Scale Imaging of Electrochemical Lithiation in Silicon.

Two-phase electrochemical lithiation in amorphous silicon

Lithium Diffusion in Silicon and Induced Structure Disorder: A Molecular Dynamics Study

Sandwich-Lithiation and Longitudinal Crack in Amorphous Silicon Coated on Carbon Nanofibers

Energetics of hydrogen/lithium complexes in silicon analyzed using the Maxwell construction

Deformation and failure of lithiated Si electrodes of Li-ion batteries

First principles simulations of the electrochemical lithiation and delithiation of faceted crystalline silicon

Atomistic Mechanisms of Phase Boundary Evolution during Initial Lithiation of Crystalline Silicon

Multi-Scale Simulation Of The Stability And Diffusion Of Lithium In The Presence Of A 90 Degrees Partial Dislocation In Silicon

Molecular dynamic investigation of the structure and stress in crystalline and amorphous silicon during lithiation

Pressure-sensitive Plasticity of Lithiated Silicon in Li-ion Batteries

Lithiation of SiO2 in Li-ion Batteries: in Situ Transmission Electron Microscopy Experiments and Theoretical Studies.

Electronic origin for the phase transition from amorphous LixSi to crystalline Li15Si4

Lithiation-delithiation cycles of amorphous Si nanowires investigated by molecular dynamics simulations

Multi-Scale Simulation Of Lithium Diffusion In The Presence Of A 30 Degrees Partial Dislocation And Stacking Fault In Si

Molecular Dynamic Behavior of Lithium Atoms in a Flat Silicene Pore on a Copper Substrate

Electron-rich driven electrochemical solid-state amorphization in Li-Si alloys

Numerical investigation of microstructure and failure of lithiated silicon under biaxial tension

Link between anisotropic electrochemistry and surface transformations at single‐crystal silicon electrodes: Implications for lithium‐ion batteries

Kinetics and Fracture Resistance of Lithiated Silicon Nanostructure Pairs Controlled by Their Mechanical Interaction